奈米結構氫氧化鎳之摻雜改性及其對鎳氫電池性能的 改善及機制研究(2/3) (NSC92-2216-E-002-006) 摘要: 本計畫的第二年延續上期研究，由化學共沉澱方式製得奈米結構Ni(OH)2活 性材料，亦採用 Co、Zn 元素對奈米 Ni(OH)2材料進行摻雜改性（Doping modification），改變Co添加物的含量，以進一步提高鎳氫電池鎳正極之電化學 導電度。由X-ray繞射和掃瞄式電子顯微鏡分析結果顯示，發現隨Co含量增加， 活性物質面積增加，這對粉末電性是有益的。由充放電實驗及交流阻抗分析可以 發現Co含量愈高，Ni(OH) 2正極之電性能亦提高。 關鍵詞: 氫氧化鎳，化學共沉澱法，鈷添加物。 Abstract The positive electrode active materials of Ni(OH) powders for alkaline Ni-MH 2 battery have been fabricated by a chemical precipitation method. The characteristic properties of Ni(OH)2 powders were analyzed by the XRD and SEM. The electrochemical properties of Ni(OH)2 powders were also analyzed by the galvanostatic charge-discharge test and AC impedance spectroscopy. In general, it must be noted that a nickel hydroxide electrode with the addition of cobalt hydroxide shows much better electrochemical properties. It was observed that the electrochemical properties of nickel cathodes depend on the contents of cobalt additive. It was indicated that the Ni-MH batteries have good performance of charge and discharge characteristics. Keywords: Ni(OH)2 , chemical precipitation method, cobalt additive 前言： 近幾年，鎳氫電池與鋰離子二次電池的市場急速的擴大。由於鋰離子電池有 著高工作電壓（3.6 V）以及高能量密度（130 Wh / kg）等優點，即使價格較高 且危險性較大，鋰離子電池仍然佔有大部分筆記型電腦與手提式電話的市場。然 而在需要高速率充放電、高循環壽命、安全性高及價格便宜的情況之下，鎳氫電 池仍是獨占鼇頭，如免插電式電鑽等大功率工件或電動汽機車。 發展電動車的瓶頸在於可充電電池，而目前公認鎳氫電池在性能上可能是最 佳的選擇，鎳氫電池是結合了鎳鎘電池、燃料電池、儲氫合金三種近代技術發展 而成 ; 正極材料為原本鎳鎘電池中正極的氫氧化鎳，負極採用氫氧燃料電池之 負極的原理，並利用儲氫合金吸放氫性能融合而成，鎳氫電池具有技術純熟、製 程穩定、無公害及高能量密度等優點，更重要的是在價格、安定性、耐過充放電 能力上具有相當大的競爭力。 研究目的： 過去針對鎳氫電池中儲氫合金負極的相關研究，已大幅提升了電池的電性， 然而整顆電池的電容量大小卻是由正極的電容所決定的，所以對正極電性的研究 是刻不容緩的。 本實驗室去年採用 Co、Zn 元素對奈米結構 Ni(OH)2 材料進行摻雜改性 （Doping modification），去年已合成出性質頗佳的奈米Ni(OH)2 粉末，並進行基 本的電性測試，發現球磨後的不規則形粉末接觸電阻較大。