CSiC摩擦材料的制备及摩擦磨损性能-ResearchGate.PDF

See discussions, stats, and author profiles for this publication at: /publication/289443524 Preparation and tribological properties of C/SiC friction materials Article  in  Journal of Inorganic Materials · July 2006 CITATIONS READS 11 70 5 authors, including: Shangwu Fan Ling Fang Cheng Northwestern Polytechnical University Kaohsiung Medical University 69 PUBLICATIONS   626 CITATIONS    89 PUBLICATIONS   417 CITATIONS    SEE PROFILE SEE PROFILE Some of the authors of this publication are also working on these related projects: C/SiC brake materials View project Juanli Deng View project All content following this page was uploaded by Shangwu Fan on 09 January 2018. The user has requested enhancement of the downloaded file. 第21卷第4期 无机材料学报 of Materials 2006年7月 Journal Jul．，2006 Inorganic 文章编号：i000—324X(2006)04—0927—08 C／SiC摩擦材料的制备及摩擦磨损性能 范尚武，徐永东，张立同，成来飞，楼建军 (西北工业大学超高温结构复合材料国防科技重点实验室，西安710072) 摘要： 通过化学气相渗透法(CVI)结合反应熔体浸渗法(RMI)制备了低成本、高性能的 C／SiC飞机摩擦材料，并模拟飞机正常着陆条件进行了摩擦磨损实验．实验结果表明：C／SiC 是比c／c更优的飞机摩擦材料，具有动、静摩擦系数高(分别为o．34、o．41)，湿态几乎无衰 减(约2．9％)，磨损小(约1．9#m／次)，摩擦性能稳定等特点．并采用金相显微镜、扫描电镜等对 C／SiC摩擦材料的摩擦面以及磨屑形貌进行了观察，并对其磨损机理进行了探索．结果表明， 磨损机理以磨粒磨损为主，同时由于垂直于摩擦面的纤维束增强了其层间抗剪切能力，从而提 高了其抗磨损性能． 关键 词：C／SiC；摩擦材料；摩擦磨损性能 中图分类号：TB332文献标识码：A 1引言