钴铬钼多孔关节烧结工艺的研究-IngentaConnect.PDF

48 / 2011 6 Study on Sintering Process of Porous Co- Cr-Mo Alloy for Artificial Joint 1 1 2 2 , , , ( 1 , 100095; 2 , 10008 ) 1 1 2 2 QIA O Zhen , HE Juan , HUANG Yong-ling , LI Guo-hua ( 1 Baimtec M aterial Co., Ltd., Beijing 100095, China; 2 School of Mechanical Electronic Information Engineering, China U niversity of M ining T echnology , Beijing 10008 , China) : A , 1280 , ; B 1280 , 1200 ; C ; D 1200~ 1240 , ; : B , , M C , 2 6 , : ; ; + + : T G 146. 1 6; T G1 2. 2 : A : 1001-4 81( 2011) 06-0048-04 Abstract: On the basis of moderately increasing sinter temperature to insure the bond strength be- tw een beads and joints, the microstructure and mechanical properties of casting Co-Cr-Mo alloy joints under different cooling regime w ere priority investigated. Group A of castings w ere vacuum sintered at 1280 and furnace cooled after original solution treatment. Group B w as directly vacuum sintered at 1280 and furnace cooled to 1200 , finally cooling to room temperature w ith flow ing Ar atmosphere. Group C slow ly cooled in casting die w ithout heat treating . Group D w as solution treated betw een 1200- 1240 and oil cooled. All above of them w ere as contrast samples w ith each others. T he results show ed that mechanical