现代表面工 程学导论——热喷涂篇电弧喷涂知识内容.pptVIP

3.5 电弧喷涂Arc Wire Thermal Spray Process;喷嘴端部成一定角度的连续送进的两根金属丝分别与直流的正负极相连接----- 使两根金属丝间产生电弧，将两根金属丝端部同时熔化，在电源作用下，维持电弧稳定燃烧； 在电弧发射点的背后由喷嘴喷射出的高速压缩空气使熔化的金属脱离金属丝并雾化成微粒 在高速气流作用下喷射到基材表面而形成涂层。;3.5.2．电弧喷涂的特点;3.5.3．电弧喷涂设备与工艺;增强的电弧喷涂涂层;Arc Sprayed Coatings;Arc Sprayed Coatings;Arc Spray Coatings;Arc Spray Coatings; ;3.6. 等离子喷涂工艺;Requirements for a Typical Plasma Spray System ;等离子工艺特点;等离子喷涂工艺;优点 可喷涂材料广泛 工艺成本低 沉积效率高 操作简单 涂层致密 喷涂效率高 ;Plasma Spray Coating Photomicrographs;Plasma Spray Chromium Oxide Coating;Plasma Spray Chromium Oxide Coatings 2.;Plasma Spray Chromium Oxide Coatings 3.;Plasma Sprayed Chromium Coating The microstructure shows a very dense coating with microhardness values in excess of 1500 HV/1kg ;Plasma Sprayed Tungsten Carbide;Plasma Spray Coating MicrostructureCeramic Coatings;Carbon fibre reinforced polymer tubes thermal spray coated with: - WC/10Co/4Cr - NiCrBSi - Chromium oxide - Alumina /3% titania Glass fibre reinforced polymer plasma sprayed with chromium oxide;Carbon fibre reinforced polymer plasma sprayed with grey alumina;Plasma Spray Tungsten Carbide / Cobalt Chromium Coating on Carbon Fibre Reinforced Polymer Composite Substrate ;Plasma sprayed zirconia yttria ceramic thermal barrier coating showing delamination problem due to excessive deposit thickness per pass ; 3.7 热喷涂预处理 是喷涂工艺中一个重要工序;1．基体表面的清洗、脱脂;（3）蒸气清洗法：蒸气清洗法是采用三氯乙烯蒸气进行清洗，尽管这种方法的清洗效果很好，但是对人体有一定的危害。 （4）对疏松表面的清洗、脱脂：对疏松表面（如铸铁件）的清洗、脱脂是比较困难的。尽管油脂不在工件表面，但在喷涂时，由于基体表面的温度升高，疏松孔中的油脂就会渗透到基体表面，对涂层与基体的结合极为不利。因此，对疏松基体表面，经过清洗、脱脂后，还需要将其表面加热到250℃左右，尽量将油脂渗透到表面，然后再加以清洗。 ;2．基体表面氧化膜的处理 ;3．基体表面的粗化处理 ;（2）机械加工法;（3）化学腐蚀法;4．基体表面的预热处理 ;5．非喷涂表面的保护 ;6、热喷涂涂层后处理和涂层性能的检验 ;（2）热喷涂涂层性能的一般检验 ;（3）涂层与基体表面的结合强度试验