硫酸盐侵蚀后砂浆的力学性能试验研究-结构工程专业论文.docxVIP

STUDY STUDY ON MECHANICAL PRoPERTIES oF MoIUAR WHICH IS ATTACKED BY TEST ABSTRACT Sulfate corrosion is one of important factors that influence the duration of concrete．Aim at this problem，this paper carries out microcosmic studies on mortar,which iS in sulfate environment,by means of tests．And several results have been gained as follow： 1．This paper carries out uneasily compression on samples of different watcr-eement ratios and corrosion degrees．Through analyzing compressive strength，modulus of elasticity and strain，laws of mechanical parameters coinciding with corrosion degrees are revealed． 2．Through uneasily fatigue tests，trends of modulus of elasticity coinciding witll the peak strain in every block cycle during the periods of exerting load and discharging load are concluded．In addition，wetting-drying cycles test are exerted on samples immerged in sulfate solution，after wetting-drying cycles，velocities of acoustic emission signals and modulus of elasticity in samples are measurated．And this paper has analyzed laws of velocity and modulus ofelasticity coinciding with corrosion degrees． 3．Furthermore，this paper uses segmented damage curve modal to fitting dates，and finds that damage parameter by fitting can reflect corrosion degrees to some extent．Based on the definition of damage，damage qualities will decrease coinciding with the increasing of corrosion degree． 4．This paper also collects acoustic emission signals during the whole process ofuneasily compression。Based on the mechanism ofacoustic emission and the characters of deformation，this paper carves acoustic emission curves into into four periods，and describes characters of each period．In addition，In addition mercury experimental has been carried out on samples of different degrees，variation law of macrocosmic mechanical properties are explained further through microcosmic scale． KEY WORDS：mortar：sulfate；acoustic emission：computerized tomography Ill 广西大学学位论文原创性声明和使用授权说明原创性声明 广西大学学位论文原创性声明和使用授权说明 原创性声明 本人声