机壳外表面用弹性手感涂料配方设计及应用.doc

7.6 机壳外表面用弹性手感涂料的配方设计及应用 周荣华 （深圳市天健（集团）股份有限公司，广东深圳518122） 摘要：通过选用合适的弹性树脂为主体，配合助剂和固化剂的选择进行配方设计，阐述了弹性手感涂料的配制及其施工工艺。测试结果表明该涂料具有附着力佳、手感细腻滑爽、抗划伤力强、优异的耐腐蚀等性能。 关键词：弹性手感涂料；双组分涂料；橡胶涂料 中图分类号：TQ630 文献标识码：A 文章编号：1006-2556（2008）08-0045-04 Formula design and use of elastic-feeling coatings for machine casing Zhou Ronghua (Shenzhen Tonge Group Co., Ltd., Shenzhen 518122,Guangdong Province Abstract: This paper narrates the preparation and formula design of elastic-feeling coatings form the selection of elastic matrix resin and additives and curing agent; and narrates the application technology. The results shows that the coatings are of good adhesion, fine and smooth feeling, excellent scratch resistance and anticorrosion property. Keywords: elastic-feeling coatings, two-package coatings, coatings for rubber 前言 如今对日用品的外观效果要求越来越高,如铝粉效果﹑裂纹效果﹑弹性手感效果等等,特别是一些经常用手触摸的部位,要求喷涂弹性手感涂料,如吹风筒手柄﹑MP3外壳﹑鼠标﹑手机外壳﹑望远镜﹑伞柄等等,使人感觉到一种软绵绵爽滑的感觉,为此弹性手感涂料应运而生. 弹性手感涂料又称橡胶涂料，现在主要是双组份溶剂型产品：一组份是带羟基的直链聚酯树脂或带羟基有少许支链的改性聚酯树脂；另一组份是异氰酸酯类固化剂,一般是用HDI三聚体型或缩二脲型。溶剂型单组分涂料，UV固化涂料，水性涂料，由于其性能及价格问题，在中国市场上应用较少。 试验部分 弹性手感涂料制造原理 要使聚氨酯涂料具备有高度弹性，则其结构必须是由线型长链大分子组成（分子量范围在几百至几千的各种类型树脂均不能显现出高弹性），并具有适度的交联（或称硫化）。线型大分子间存有弱的分子间力，在常温是柔顺无规线团，能够移动或转动。在柔性链段之间需有短的刚性链段，示意式如下： O ?? H H H 〔--（-R-N-C-O-(G)-O-C-N--〕M—(R-N-C-O~~长链~~ O-C-N--)n〕 H ?? ?? ?? O O O 上式中，短节的二元醇（G）所生成的氨酯链段呈刚性，在分子间氢键吸力大，可起到弱的交联点的作用，而长链部分的链段柔软。刚性部分的数量决定涂料膜的硬度和高温性质。柔软部分的数量决定涂料膜的弹性、低温性质、耐水解性、耐溶剂性。 1．2 试验用原材料 弹性手感涂料主要是由弹性树脂﹑固化剂﹑催干剂﹑消光粉﹑弹性粉﹑手感助剂﹑有机溶剂等组成，本试验研究所采用原材料见表1。 表1 弹性手感涂料所用原材料及产地/产商 原材料名称 型号 产地/产商 弹性树脂 1650 拜耳 弹性树脂 5800-X-70 长润 弹性树脂 317 盖斯塔夫 手感弹性浆 558 德国