材料与试验协会 B9-90（2003）青铜制电车架空线.PDFVIP

Designation: B 9 – 90 (Reapproved 2003) Standard Specification for Bronze Trolley Wire1 This standard is issued under the fixed designation B 9; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval. 1. Scope 4.2 Tests on a specimen of round wire containing a joint 1.1 This specification covers round, grooved, and figure-9 shall show at least 95 % of the tensile strength specified in deep-section grooved bronze trolley wire. Table 1. Elongation tests shall not be made on specimens 1.2 The bronze trolley wire may be made in any of the three containing joints. distinct alloys indicated in accordance with their increasing 4.3 Tension tests shall be made on representative samples. conductivities: Alloy 40, Alloy 55, Alloy 80. The elongation shall be determined as the permanent increase 1.3 The values stated in inch-pound units are to be regarded in length, due to the breaking of the wire in tension, measured as the standard. The metric equivalents of inch-pound units between gage marks placed originally 10 in. (254 mm) apart given in this standard may be approximate. upon the test specimen (Explanatory Note 2). The fracture shall be between the gage marks and not closer than 1 in. (25.4 mm) 2. Orde