火电厂小径管管座角焊缝的无损检测-中国大唐集团公司.pdf

2014 论文汇编 火电厂小径管管座角焊缝的无损检测 雒焕胜 （兰州西固热电有限责任公司） 摘 要：火力发电厂有很多小径管管座角焊缝，由于其结构特点和工况的影响，焊缝上往往 会产生较大的应力，容易产生缺陷，有关规程也对此类焊缝的检测做了明确规定。火力发电 厂目前对这种角焊缝的检测通常采用表面检测和内部检测两种方法，表面检测中磁粉检测时 要注意磁化角度和提升力，内部超声检测对于小径管管座角焊缝来说目前还没有具体的标准 可以依据，需要根据具体部件，采取合理的小径管超声检测方法来确定缺陷。 关键词：小径管；管座角焊缝；损坏原因；无损检测 [Abstract] Thermal power plant has a lot of small tube fillet welding seats, as a result of its structural characteristics and working conditions, weld tend to produce larger stress, prone to defects, regulations also detection of such welds made specific provision. Thermal power plant at present on the fillet weld detection usually adopts the surface detection and detection of two kinds of methods, surface of the magnetic particle testing to the attention of the magnetization angle and lifting force, internal ultrasonic detection of fillet welding seats, there is no specific standard can be the basis for small tube, according to specific components, adopt the reasonable path pipe ultrasonic detection method to identify defects. [Keywords] small diameter tube; fillet welds; damage; nondestructive testing 1 引言 火力发电厂有很多小径管管座角焊缝，如锅炉的疏水、受热面的管道和集箱上都有。由 于其结构特点和机组启停、运行过程中温度变化等原因，焊缝上会产生较大的应力，容易产 生缺陷，同时由于熔化焊本身也可能存在缺陷，有关规程对此类焊缝的检测做了明确规定。 火力发电厂对小径管管座角焊缝的检测通常采用表面检测为主，内部检测辅助两种方法，如 何合理的选择适当的无损检测方法，能够准确的检测出管座角焊缝的缺陷，需要根据具体部 件加以具体的检测方法来确定。 2 管座角焊缝的结构、应力分布和损坏原因 2.1 管座角焊缝的结构 在火电厂压力容器及联箱中，汽水输送管道、仪器仪表管道，会大量出现两个圆柱体正 交或斜交相贯焊接所形成的角焊缝。为避免强制对口，在容器或联箱与接管间往往加装管座。 通常接管与筒体焊接的角焊缝形式有插入式和安放式两种。插入式管座角焊缝是接管座插入 336 2014 论文汇编 筒体内焊接