正火温度对t91成品管组织跟性能的影响资料.pdfVIP

正火温度对T91成品管组织与性能的影响 皮华春 韩静涛 刘靖 鲍善勤 倪明贵 赵跃健 北京科技大学材料科学与工程学院 100083 四川长城协和钢管有限公司 621701 摘要 本文首先测定T91 钢的过冷奥氏体连续转变 CCT 曲线 得出T91 钢的Ac3 线为905 Ac1 线温度为840 Ms 温 度为420 Mf 温度为240 并指出当冷却速度小于0.1 /s 时 冷却析出组织为铁素体和珠光体 当冷速大于等于0.1 /s 时 冷却析出组织为马氏体 最后着重研究正火温度对T91 成品管组织性能的影响 指出T91 钢管成品管热处理工艺中最佳正 火温度为 1040 左右 关键词 T91 钢 CCT 曲线 正火 组织 性能 Effect of normalizing temperature on microstructure and property of T91 tube PI Huachun HAN Jingtao LIU Jing (School of Materials Science and Engineering ,Univesity of Science and Technology Beijing 100083) BAO Shanqin NI Minggui Zhao Yuejian (Sichuan Changcheng Concord Stainless Tube Co., Ltd 621701) abstract Firstly continuous cooling transformation CCT curve of T91 steel is determined. The temperature lines of Ac3, Ac1, Ms and Mf are concluded for T91 steel, which are 905 , 840 , 420 and 240 in turn. When cooling rate is lower than 0.1 /s, the precipitated microstructure after cooling are ferrite and perlite. Otherwise the microstructure is martensite. At last Effect of normalizing temperature on microstructure and property of T91 tube is studied on focus. The best normalizing temperature of T91 tube is about 1040 . Key words T91 steel, CCT curve, normalizing, microstructure, property 1前言 T91钢是一种改进的9Cr-1Mo钢 该钢通过添加V Nb和N产生的沉淀硬化来改进9Cr-1Mo基 体钢的高温强度 该钢主要在电站工程中投入工业性使用 广泛用于大型火电机组及其配套的锅炉 中 用这种钢轧制的钢管壁温可超过600 最高可达650 蒸汽压力在24MPa以上 并显示出了 优异的综合性能 T91钢管的生产工艺一般是热轧 冷轧和成品管热处理 正火 回火 成品热处 理是钢管在最后一个冷变形道次 成品道次 结束后进行的热处理 它除了能够消除加工硬化和残 [1] 余应力外 还能使钢管获得所需要的综合性能 根据钢的过冷奥氏体连续冷却转变曲线 CCT曲线 [2]