成孔剂对烧结页岩砖性能的影响.docVIP

PAGE PAGE 1 成孔剂对烧结页岩砖性能的影响 　　摘要：选用锯末、煤矸石和造纸污泥作为烧结页岩砖的成孔剂，系统研究不同成孔剂的热解特性及其对页岩烧结砖的可塑性、体积密度、抗压强度、显孔隙率、吸水率等性能的影响。结果表明：随着锯末掺量的增加，烧结砖中孔隙数量增加，同时其体积密度和强度迅速下降，吸水率增加，因而掺量应控制在6%以内；煤矸石可塑性较差，烧失量较小，烧结页岩砖的孔隙率低，从而导致其吸水率低，体积密度和强度降低幅度都较小，实际生产中可根据内燃砖发热量和可塑性要求，适量掺加煤矸石；造纸污泥的可塑性较好，随着掺量增加混合料的可塑性变大，但掺量过大成型搅拌困难且烧结砖的收缩大，强度降幅大，吸水率大，因而掺量应不超过7%。 　　关键词：烧结页岩砖；成孔剂；可塑性；热解特性 　　中图分类号：TU522.1文献标志码：A文章编号：1674-4764（2012）02-0149-05 　　InfluenceofPore-formingAgentsonthePropertiesofSinteredShaleBrick 　　XIEHou-li1,2,PENGJia-hui1,ZHENGYun1,CHENYan1 　　(1.CollegeofMaterialScienceandEngineering,ChongqingUniversity,Chongqing400045,P.R.China; 　　2.ConstructionTechnologyDevelopmentCenterofChongqing,Chongqing400015,P.R.China) 　　Abstract:Sawdust,coalgangueandpapersludgewerechosenaspore-formingagentsofsinteredshalebrick.Thepyrolysisbehaviorsofdifferentformingagentswerestudiedandtheinfluencesoftheagentsonbulkdensity,compressivestrength,porosity,andwaterabsorptionpropertiesoftheshalebrickwerealsoinvestigated.Itisshownthat,withtheincreaseofthedosageofsawdust,porenumberofthesinteredbricksandwater-absorptionincrease,whilethevolumedensityandstrengthfallrapidly.Thus,thedosageofsawdustshouldbecontrolledwithin6%.Becauseofpoorerplasticityandlowerignitionofcoalgangueaswellaslowporosityrateofsinteredbricks,thewater-absorptionofsinteredbricksispoor,anddecreasesofdensityandstrengtharenotobvious.Inpracticalproduction,accordingtotherequirementsofbrick-makingheatandplasticity,amoderateamountofcoalganguecanbeadded.Theplasticityofthebricksimprovesasthedosageofpapersludgeincreasesduetoitsgoodplasticity.However,excessivedosageofpapersludgewillresultinlargeshrinkageofsinteredbrick,lowstrengthandhighwaterabsorption;therefore,thedosageshouldnotexceed7%. 　　Keywords:sinteredshalebrick;pore-formingagent;plasticity;pyrolysis 　　 　　传统粘土实心砖不仅毁田严重、生产耗能大，而且墙体保温性能差。国家“禁实”墙材改革的有效途径之一就是使用非粘土原料，并对实心砖进行空心化和微孔化改造，这种趋势是当前绿色建材、节能建材的发展需要［1］。空心化主要依靠增大烧结砖的孔洞率，但受模具的制作、成型设备、工艺条件、成品率等的制约，为进一步降低烧结砖的自重和提高其保温性能，国内外开始着手微孔化方面的研究。其主要途径是在砖坯中加入成孔剂，在烧结过程中砖体内可产生大量孔隙