《疲劳和断裂第七讲》.pptVIP

疲劳和断裂第七讲;用线弹性材料物理模型，按照弹性力学方法，研究含裂纹弹性体内的应力分布，给出描述裂纹尖端应力场强弱的应力强度因子K，并由此建立裂纹扩展的临界条件, 处理工程问题。; Linear elastic fracture mechanics predicts infinite stresses at the crack tip. In real materials, however, stress at the crack tip are finite because the crack tip radius must be finite. Inelastic material deformation, such as plasticity in metal , leads to further relaxation of the crack tip stress. ; 7.1 裂纹尖端的小范围屈服; 这里仅简单讨论沿裂纹线上屈服区域的大小。; 对于平面问题，还有： ?yz=?zx=0； ?z=0 平面应力 ?z=?(?x+?y) 平面应变; 将各主应力代入Mises屈服条件，得到： (平面应力) (平面应变);虚线为弹性解，r?0，?y??。 由于?y?ys，裂尖处材料屈服， 塑性区尺寸为rp。; The simple analysis as above is not strictly correct because it was based on an elastic crack tip solution. When yielding occurs, stress must redistribute in order to satisfy equilibrium. ; 为满足静力平衡条件，由于AB部分材料屈服而少承担的应力需转移到附近的弹性材料部分，其结果将使更多材料进入屈服。因此，塑性区尺寸需要修正。; 于是得到：; 依据上述分析，并考虑到平面应变时三轴应力作用的影响，Irwin给出的塑性区尺寸R为：; Most of the classical solution in fracture mechanics reduce the problem to two dimensions. That is at least one of the principal stresses or strains is assumed to equal zero (plane stress and plane strain respectively).; 2. 考虑裂尖屈服后的应力强度因子;rp;例7.1 无限宽中心裂纹板，受远场拉应力?作用， 试讨论塑性修正对应力强度因子的影响。;对于平面应力情况，?=1；若(?/?ys)=0.2，?=1%；若(?/?ys)=0.5，?=6%；当(?/?ys)=0.8时，?达15%。 对于平面应变情况，??3，二者相差要小一些。; 3. 小范围屈服时表面裂纹的K修正; 可见，小范围屈服时，表面裂纹的 K计算只须用 形状参数Q代替第二类完全椭圆积分E(k)即可。; 例7.2 某大尺寸厚板含一???面裂纹，受远场拉应力? 作用。材料的屈服应力为?ys=600MPa, 断裂韧 性K1c=50MPam1/2，试估计： 1) ?=500MPa时的临界裂纹深ac。 (设a/c=0.5) 2) a/c=0.1，a=5mm时的临界断裂应力?c；; 故得到： ;12622.8; 一般地说，只要裂尖塑性区尺寸rp与裂纹尺寸a相比 是很小的(a/rp=20-50)，即可认为满足小范围屈服条 件，线弹性断裂力学就可以得到有效的应用。; Plasticity correcting can extend LEFM beyond it’s normal validity limits. One must remember, however, that Irwin correction are only rough approximate of elastic-plastic behavior. When