一、 PTFE微孔薄膜简介 Introduction to PTFE Microporous Membrane PTFE微孔薄膜由高结晶度的 PTFE分散料，经过挤压、纵向拉伸、横向拉伸，最 终形成带有立体三维结构的薄膜。其孔径在 0.02～5um 之间，薄膜厚度在 8～ 30um，孔隙率在 80～97%之间。 PTFE micro-porous membrane is made up of high crystallinity PTFE fine powder and shaped into 3D structure through compressing, vertical and horizontal stretching. The membrane pore size is between 0.02~5 μm, thickness is 8~30 μm and porosity is between 80~97%. 金由 iTEX高性能 PTFE微孔薄膜特点 金由 iTEX高性能 PTFE微孔薄膜在生产之初，严格控制 PTFE分散料品质。配合 18 年 PTFE微孔薄膜的生产经验，在生产过程中，对于细节精益求精。加上多处 “独到”的生产工艺，使金由 iTEX高性能 PTFE微孔薄膜具有高耐水压力、高透 湿性、高机械强度等性能。 Features of Jinyou iTEX PTFE membrane The PTFE fine powder is controlled strictly before to be used as approved material. And thanks to our 18-year experience and unique technology in producing PTFE membrane, we have consistently improved the product in every detail. Therefore, iTex membrane is featured by high water resistance, high breathability and high durability. 高耐水压力：在 20 次水洗以后，按美国 ASTMD751 2006‐ 标准测定： C 型达 20,000mm 耐水压力。 S 型可达 67,000mm 耐水压力，已达美国 MIL ‐DTL31011B‐ 水平（美国军方标准） ，特别适用于军、警、消防官兵服装。 High Water Resistance According to ASTMD7751-2006, water resistance for type C reaches 20,000mm H 2O and Type S reaches up to 67,000mm H O after 20 times washing, which meets the standard of US 2 MIL-DTL-31011B. Therefore, it becomes ideal material to make uniforms for army, police and firefighting. 高透湿 / 透气性：洗涤前透湿量（汗液形成的水蒸气）按日本标准 JISL099B1标准 测试， C型达 5000g/m2 ·24h以上,S型达 7500g/m 2 ·24h以上。 High breathability / Air Permeability 2 According to JISL099B1, the moisture breathability for Type C reaches over 5000g/m ·24h