冻融循环作用下表层嵌贴CFRP混凝土界面黏结性能试验研究（历史学毕业论文）.docVIP

冻融循环作用下表层嵌贴CFRP混凝土界面黏结性能试验研究（历史学毕业论文） 文档信息 属性： F-0181BM，doc格式，正文9967字。质优实惠，欢迎下载！ 适用： 作为文章写作的参考文献，解决如何写好实用应用文、正确编写文案格式、内容摘取等相关工作。 目录 TOC \o 1-9 \h \z \u 目录 1 正文 1 搞要 1 关键字：表层嵌贴；CFRP；黏结性能；冻融循环；混凝土 2 1 试验方案 5 2 试验结果及分析 6 参考文献 11 论文原创声明（模板） 13 论文致谢（模板） 13 正文 冻融循环作用下表层嵌贴CFRP混凝土界面黏结性能试验研究（历史学毕业论文） 搞要 摘要：摘要：以嵌贴CFRP-混凝土黏结的冻融耐久性为研究对象，通过拔出试验考察了冻融循环作用下嵌贴FRP与具有不同强度或抗冻性能混凝土的黏结性能，讨论了冻融循环下嵌贴FRP-混凝土界面黏结的退化机理；分析了冻融循环作用下混凝土槽至试件边缘距离、胶层厚度等因素对试件界面黏结性能的影响.试验结果表明：冻融循环作用下普通C30混凝土力学性能退化显著，添加引气防冻剂和减水剂的C30混凝土强度下降显著小于普通C30混凝土，C60混凝土强度反而有所提高；冻融循环导致了嵌贴CFRP-普通C30混凝土的黏结承载力下降和破坏模式转变，但嵌贴CFRP与抗冻混凝土间的黏结承载力没有显著降低，表明混凝土冻融损伤是冻融循环下嵌贴FRP-混凝土黏结退化的主要原因；槽壁厚度较小时，加载端槽壁混凝土出现锥形斜裂缝；胶层厚度较薄时，冻融循环作用下试件黏结承载力的降低较胶层较厚的试件更为显著 关键字：表层嵌贴；CFRP；黏结性能；冻融循环；混凝土 中图分类号：TU378 文献标志码：A 文章编号：1674-2974（2017）05-0063-10 Abstract：The durability of the interface between NSM FRP and concrete under freeze-thawing cycles was examined. The pull-out tests were conducted to investigate the influence of freeze-thawing cycles on the bond performance between NSM FRP and concrete with normal strength， high strength， or additional frost resistance. The mechanism of the bond degradation between NSM FRP and concrete under the freeze-thawing cycles was also discussed. Moreover， the influences of the distance between concrete edge and groove （edge distance） and the thickness of epoxy adhesive on the bond durability of the NSM FRP were studied. The test results show that freeze-thawing cycling resulted in the strength deterioration of ordinary concrete， while the high strength concrete and the concrete with frost resistance showed no significant deterioration under freeze-thawing cycles. Freeze-thawing cycling also caused the transformation of failure mode and the relatively significant decrease in bond capacity for specimens using ordinary concrete. Nevertheless， it had no substantial impact on the bond performance of specimens made by concrete with high strength or frost resistance. This result indicates that the bond deteriora