PAGE 22 题目：自修复涂料的制备及研究 自修复涂料的制备及研究 摘要 自修复涂料是当涂膜受到损坏后具有自修复功能，能在涂层破损时发挥自愈作用。将微胶囊技术应用于自修复涂层材料中对延长涂料使用寿命，降低维修维护成本具有重大意义。 本文以EA/TPGDA为囊芯，脲醛树脂为囊壁，采用原位聚合法合成了自修复微胶囊。同时，对自修复微胶囊的应用进行了初步研究，将微胶囊埋植入树脂防腐涂料中并涂刷于金属表面进行腐蚀试验，采用数码相机观察了微胶囊芯壁比、用量对金属防腐涂层耐腐蚀性能的影响规律，并评估了自修复涂层的自修复性能。实验结果表明，当微胶囊芯壁比为2:1，用量占涂料用量10%时，微胶囊的耐腐蚀性能最好，自修复效果明显。 关键词：自修复；微胶囊；原位聚合法；防腐涂料 Prepare and Research of Self-healing Coating Abstract Self-healing coating is damaged when the film has a self-healing capabilities, can play a role in self-healing coating damage. The microencapsulation technology for self-healing coating material of great significance to extend paint life, lower repair and maintenance costs. In this paper, EA / TPGDA as core, urea-formaldehyde resin wall, using the in situ polymerization synthesis of self-healing microcapsules.Meanwhile, the application of self-healing microcapsules were studied, the microcapsules implanted buried resin anticorrosive coating and paint on the metal surface corrosion test, using a digital camera to observe the core microcapsule wall ratio, the amount of anti-corrosion coating for metals layer of corrosion influence of energy, and to assess the self-healing coating of self-healing properties.Experimental results show that when the core microcapsule wall ratio of 2:1, with 10% accounted for the amount of paint, microcapsules best corrosion resistance, self-healing effect. Key words: Self-healing; Microcapsule; Situ polymerization; Anti-corrosion coating 目 录 TOC \o 1-3 \h \z \u 1 绪 论 1 1.1 自修复功能材料 1 1.1.1 原理和方法 1 1.1.2 自修复材料中自愈合聚合物简介 2 1.2 微胶囊技术简介 3 1.2.1 微胶囊概念及形态结构 3 1.2.2 微胶囊的功能和应用 3 1.2.3合成微胶囊原料的选择 4 1.2.4 合成微胶囊方法的选择 5 1.2.5 微胶囊的结构性能及其表征方法 5 1.3 自修复微胶囊技术 6 1.3.1 自修复微胶囊应具备的条件 6 1.3.2 微胶囊自修复技术应用于涂料的研究进展 6 1.4 本论文的研究背景、研究意义和研究内容 7 1.4.1 本论文研究的背景及意义 7 1.4.2 本论文的主要研究内容 7 2 实验部分 8 2.1 实验原料及仪器设备 8 2.2 EA/TPGDA微胶囊的合成 8 2.3 自修复微胶囊的表征 9 2.3.1 微胶囊的形貌表征 9 2.3.2 微胶囊产率的测定 9 2.4 漆膜的制备 10 2.5