(7359)--河道淤泥制备免烧结砖性能研究.pdfVIP

河道淤泥制备免烧结砖性能研究 摘  要：探究了河道淤泥的建材化用途以及生产淤泥免烧砖的配方，对配方筛选过程中出现的试块开裂和激发剂掺量的选择展开了 深入分析。在此基础上，加入淤泥取代胶凝组分，对强度变化及其机理进行探讨。 关键词：淤泥免烧砖；开裂；激发剂掺量；强度 中图分类号：TU5               文献标志码：B                 文章编号：1006-2890（2020）04-0017-04 Study on Performance of Non-sintered Bricks Prepared with River Silt Chen Zhuorui，Yang Zhengxian，Zhang Yong，Shi Peng * College of Civil Engineering，Fuzhou University，Fuzhou，Fujian 350108 Abstract： In this paper， application of river silt for building materials and the recipe of non-sintered bricks with river silt are experimentally  studied. In the formulation of the recipe the sample cracking and activator dosage are analyzed in depth. Accordingly， the cement was  partially replaced by river silt in an appropriate proportion to prepare non-sintered bricks. Strength changes of the non-sintered bricks with  the activator dosage， as well as the mechanisms hidden behind， are discussed eventually. Key words ： Non-sintered river silt brick； Cracking； Activator dosage； Strength 1  引言 了在淤泥中掺入不同的物质对最终烧结砖强度的影响，最终发 福建的河网密度大，境内河流总长度约1.3万km，河网密 现掺入10%的页岩以及掺入10%的砖粉的烧结砖成型性较好， 度每平方公里超过0.1 km。每条河流的河床上都会随时间的推 也有较高的强度和耐久性，但是在掺入2%的煤粉灰组别各项 ［7］ 移而沉积有大量的河道淤泥，河道淤泥会造成河水滞流、水体 指标均下降；蒋正武 等提出了利用生物质燃料代替煤炭燃料、 浑浊甚至产生黑臭和有害的污染物沉积，严重影响周边的生态 利用河道淤泥代替粘土原料烧结制备河道淤泥多孔砖，并开发 环境。疏浚淤泥又具有含水量大的特点，在疏浚河道的清淤工 出太阳能干燥技术、烟气处理和余热利用技术；范杰、李庚英［8］ 作完成后需要经过晾晒后方可外运处理。这不仅占用了大量的 通过正交试验分析筛选最佳的再生淤泥免烧砖的配合比设计， 场地，更有可能在晾晒、露天放置的过程中影响周围空气环境、 并在实验中发现泥灰比是影响再生淤泥免烧砖强度和耐久性的 造成重金属溢出以及二次污染晾晒土地等问题。福建省如此密 最主要因素，且3：1时为最佳泥灰比。 集河流网使得福建清淤疏浚、处理淤泥工作变得尤为重要和迫 上述几种主要的淤泥建材化资源再利用方法中，制造陶粒 切。因此，寻找一种能大量处理淤泥、创造经济效益的解决办 和烧结砖需要消耗大量的燃料资源，制造成本较高；在利用淤 法成为河流疏浚和改造环