铁尾渣对水泥生料易烧性及熟料的影响.pdfVIP

2023年1月 江西建材 试验与研究 铁尾渣对水泥生料易烧性及熟料的影响 吴金国 江西省华恒工程检测有限公司，江西 南昌 330001 摘要：针对钢铁厂铁尾渣产量大和利用率低的问题，利用铁尾渣含铁量高的特点，用铁尾渣作为铁质原料烧制水泥熟料。在最高 燈烧温度为1400℃时，掺入铁尾渣后，烧制的熟料中f-CaO含量较低。用烧制的熟料磨细制成的水泥各项性能符合GB175-2007 《通 用硅酸盐水泥》P·I42.5硅酸盐水泥的要求，部分样品达到了P·I52.5硅酸盐水泥的要求。掺入铁尾渣不会影响熟料的矿物形成， 熟料岩相、矿物组成和结构均较好。 关键词：铁尾渣；易烧性；力学性能 中图分类号：TU528 文献标志码：B Effect of Iron Tailings on Burnability / of Cement Raw Material and Clinker WuJinguo Jiangxi Huaheng Engineering Testing Co. Ltd., Nanchang, Jiangxi 330001 Abstract : Aiming at the problems of large output and low utilization rate of iron tailings in iron and steel works,iron tailings are used as iron raw materials to fire cement clinker. When the highest calcining temperature is 1400°C ,the content of f-CaO in the clinker mixed with iron tailings is lower.Various properties of the cement ground fine with the fired clinker meet the requirement of P- I 42.5 Portland cement in GB175-2007 General Portland Cement, and some samples are in gear with P. I 52.5 Portland cement .The addition of iron tailings does not affect the mineral formation of clinker, and the clinker lithofacies mineral composition and structure are good. Key words: Iron tailings ; Burnability; Mechanical property 0 引言 表1 试验原材料的化学组成质量分数 % 随着工业化进程不断地加快，我国对于钢铁资源的需求 名称 烧失量 SiO2 Al,0; Fe20; Cao MgO 日益旺盛，但国内大部分钢铁厂都面临着铁尾渣无处堆放的问 石灰石 42.64 1.97 0.57 0.35 51.48 0.48 题。为实现钢铁行业的绿色发展，对于钢铁厂的铁尾渣进行资 源化利用势在必行[1-4]。现阶段，铁尾渣的资源化利用率仍然 千枚岩 5.98 62.05 18.26 8.17 0.62 0.75 偏低，用于建材行业中的研究更少。因铁尾渣具有一定的火山 铁尾渣 -2.78 29.87 5.79 55.51 1