AlCoCrFeNiTix高熵合金铸态及不同温度退火后组织和性能研究的中期报告.docxVIP

AlCoCrFeNiTix高熵合金铸态及不同温度退火后组织和性能研究的中期报告 摘要： 本次研究针对AlCoCrFeNiTix高熵合金，分别研究了其铸态和经不同温度退火后的组织和性能。利用扫描电镜、X射线衍射和硬度试验等手段对不同状态下的合金进行了表征。 结果表明，AlCoCrFeNiTix高熵合金在铸态下为均质的面心立方结构，退火后形成了多相结构。随着退火温度的升高，合金中的析出相逐渐增多，出现了石墨化的样貌。合金的硬度也随着退火温度的升高而逐渐降低。 基于以上结果，可以得出结论：AlCoCrFeNiTix高熵合金在铸态下为均质的面心立方结构，经过不同温度的退火后形成了多相结构，其中析出相逐渐增多并呈现出石墨化的样貌。硬度随着退火温度的升高而逐渐降低。 关键词：AlCoCrFeNiTix高熵合金；铸态；退火；组织；性能 Abstract: In this study, the microstructure and properties of AlCoCrFeNiTix high-entropy alloy in the as-cast state and after annealing at different temperatures were investigated. Scanning electron microscopy, X-ray diffraction, and hardness testing were used to characterize the alloy in different states. The results showed that the AlCoCrFeNiTix high-entropy alloy had a homogeneous face-centered cubic structure in the as-cast state and formed a multiphase structure after annealing. With the increase of annealing temperature, the precipitated phases in the alloy increased gradually, showing a graphitic appearance. The hardness of the alloy also decreased gradually with the increase of annealing temperature. Based on the above results, it can be concluded that the AlCoCrFeNiTix high-entropy alloy has a homogeneous face-centered cubic structure in the as-cast state and forms a multiphase structure after annealing at different temperatures, in which the precipitated phase gradually increases and shows a graphitic appearance. The hardness decreases gradually with the increase of annealing temperature. Keywords: AlCoCrFeNiTix high-entropy alloy; as-cast state; annealing; microstructure; properties.