涉海抗菌耐蚀性TiO2复合薄膜的制备及其性能研究的中期报告.docxVIP

涉海抗菌耐蚀性TiO2复合薄膜的制备及其性能研究的中期报告 摘要 本报告介绍了一种制备涉海抗菌耐蚀性TiO2复合薄膜的方法，并对其性能进行了研究。该复合薄膜采用溶胶-凝胶法制备，以氟聚酰亚胺为载体，将TiO2和纳米银掺杂于载体中。经过热处理和紫外光照射，制备出具有优异涉海抗菌性和耐蚀性的复合薄膜。采用扫描电子显微镜（SEM）、X射线衍射仪（XRD）、傅里叶变换红外光谱仪（FTIR）和紫外-可见分光光度计等方法对复合薄膜的形貌、结构及物化性质进行了表征。结果表明，制备的涉海抗菌耐蚀性TiO2复合薄膜在500小时的海洋暴露实验中，表现出了优异的抗菌性和耐蚀性，适合应用于海洋工程领域。 关键词：TiO2；涉海抗菌；耐蚀；复合薄膜。 Abstract This report introduces a method for preparing TiO2 composite films with antibacterial and corrosion resistance properties in seawater, and studies its properties. The composite film was prepared by sol-gel method, using fluoropolyimide as carrier, and TiO2 and nano-silver were doped in the carrier. After heat treatment and UV light irradiation, a composite film with excellent seawater antibacterial and corrosion resistance was prepared. The morphology, structure and physicochemical properties of the composite film were characterized by scanning electron microscope (SEM), X-ray diffraction (XRD), Fourier transform infrared spectrometer (FTIR) and UV-visible spectrophotometer. The results show that the prepared TiO2 composite film with antibacterial and corrosion resistance in seawater has excellent antibacterial and corrosion resistance in the 500-hour marine exposure experiment, which is suitable for application in the field of marine engineering. Keywords: TiO2; seawater antibacterial; corrosion resistance; composite film.