木质素基酚醛树脂木材胶粘剂的制备与性能研究的中期报告.docxVIP

木质素基酚醛树脂木材胶粘剂的制备与性能研究的中期报告 摘要： 本研究旨在制备一种基于木质素和酚醛树脂的新型木材胶粘剂，探究其制备工艺及性能。本文介绍了制备过程中的实验条件，对材料进行了表征和分析，分别测试了胶合板的强度及耐水性能。结果表明，最佳的制备温度为120℃，最佳的酚醛树脂质量分数为30%，最佳的反应时间为30min。通过对比实验，发现其性能优于传统的酚醛树脂胶粘剂，达到了一定的胶合效果，表明该新型胶粘剂具有较高的应用价值和开发前景。 关键词：木质素；酚醛树脂；胶粘剂；胶合板 Abstract: The aim of this study was to prepare a new type of wood adhesive based on lignin and phenol-formaldehyde resin, and to explore its preparation process and properties. The experimental conditions, material characterization and analysis were introduced in this paper, and the strength and water resistance of the plywood were tested， respectively. The results showed that the best preparation temperature was 120℃, the best quality fraction of phenol-formaldehyde resin was 30%, and the best reaction time was 30min. Through comparative experiments, it was found that the performance was better than that of traditional phenol-formaldehyde resin adhesive, and achieved a certain bonding effect, indicating that the new adhesive has high application value and development prospects. Keywords: lignin; phenol-formaldehyde resin; adhesive; plywood