高杂质含量钨酸钠溶液净化试验.docx

高杂质含量锦酸钠溶液净化试验

邓声华;黄泽辉;赵立夫;龚丹丹;邓登飞

【摘要】Thesodiumtungstatesolutionoutofsodiumphosphatedecompositionofscheelitecontainshighimpurities.Tosolvethisproblem,thepurifyingeffectsoffluoride,phosphorous,siliconandarsenicbybasicmagnesiumcarbonatewasstudied.Effectsofbasicmagnesiumcarbonatedosage,pHvalue,reactiontemperature,reactiontimeonimpuritiespurifyingwereresearched.Theremovalmechanismofimpuritieswasalsoresearched.Theresultsshowedthatwhenthedosageofbasicmagnesiumcarbonatewascontrolledunderthefollowingconditions,(Mg/F=0.56withpHvalue,reactiontemperatureandreactiontimerespectivelyas9and90°Cand180min,theremovalratesoffluorideandphosphorouscanreachedmorethan95%andthatofarsenicandsiliconreached36%and72%.Theimpuritiesofsodiumtungstatesolutioncanbepurifiedto:pF0.3g/L,pp0.006g/L,pAs0.02g/L,pSi0.11g/L.AnalysisshowedfluoridereactedwithbasicmagnesiumcarbonatetoformNaMgF3.%针对白钨矿磷酸钠分解液含杂质高的情况，研究了碱式碳酸镁对氟、磷、砷、硅杂质的去除效果。考察了碱式碳酸镁加入量、分解液pH、反应温度、反应时间等因素对净化效果的影响，分析了碱式碳酸镁除杂的机理。结果表明，当控制碱式碳酸镁加入量为Mg/F=0.56,pH=9，反应温度90C,反应时间180min时，氟、磷去除率大于95%，碑去除率达到36%，硅去除率达到72%。钨酸钠料液可净化至质量浓度：pF0.3g/L、pp0.006g/L、pAs0.02g/L、pSi0.11g/L,分析表明，料液中的氟与碱式碳酸镁反应形成NaMgF3。

【期刊名称】《中国钨业》【年(卷)，期】2015(000)005【总页数】4页(P64-67)【关键词】钨酸钠;碱式碳酸镁;净化;白钨矿;氟

【作者】邓声华;黄泽辉;赵立夫;龚丹丹;邓登飞【作者单位】崇义章源钨业股份有限公司，江西崇义341300;崇义章源钨业股份有限公司，江西崇义341300;崇义章源钨业股份有限公司，江西崇义341300;崇义章源钨业股份有限公司，江西崇义341300;崇义章源钨业股份有限公司，江西崇义341300【正文语种】中文

【中图分类】TF803.25白钨矿磷酸钠分解工艺已在工业上得到应用，且分解效果好［1］，但分解得到的钨酸钠料液杂质含量高，如氟质量浓度为1~7g/L,磷为0.1~0.2g/L,此外，料液中还含碑、硅等杂质元素。这些杂质元素严重影响产品质量，增加了废水处理难度。经典的镁盐沉淀法除磷、砷、硅、氟是采用MgCl2、MgSO4等可溶性镁盐沉淀杂质离子，净化效果较好。磷、碑、硅、氟可除至质量浓度pp0.007g/L、pAs0.01g/L.pSi0.04g/L.pF0.2g/L［2］。目前，国内钨冶炼普遍采用离子交换工艺，而镁盐沉淀法引入的Cl-、SO42-等阴离子极易造成树脂吸附容量下降。因此，研究采用溶解度很低的碱式碳酸镁吸附高杂质钨酸钠料液中的氟、磷、碑、硅，避免引入阴离子而降低后续离子交换工艺树脂吸附容量的情况，同时又达到净化的目的。

1.1试验试剂

试验以碱性条件下白钨矿磷酸钠分解得到的钨酸钠料液为原料，其主要化学成分及浓度如表1所示。

试验采用的碱式碳酸镁、浓硫酸、氢氧化钠、硫酸等试剂均为分析纯，钨酸为工业纯。