铲刃长度的热处理膨胀

刘强，梁平福，秦绪顺

(山东北方工程装备有限公司，山东泰安271000)

摘要：25CrMnB钢制铲刃，尺寸为长600～2500mm,宽152～203mm,厚12～25mm,要求采用喷水压淬。研究了压床压力、喷水时间、喷水压力、淬火水温对铲刃长度膨胀量的影响。结果表明，除了喷水时间外，其他淬火冷却工艺参数，特别是淬火压床的压力，均对铲刃长度的膨胀量有明显的影响。

关键词：铲刃；热处理；膨胀系数

中图分类号：TG162.2文献标识码：B文章编号：1008-1690(2015)01-0042-04LengthIncrementResultingfromHeatTreatmentfortheShovelingBlade

LUQiang,LIANGPingfu,QINXushun

(ShandongNorthEngineeringEquipmentCo.,Ltd.,Taian271000,ShandongChina)

Abstract:Akindofshovelingblade,madeof25CrMnBsteel,and600to2500mmlongby152to203mmwideby

12to25mmthick,istobehardenedbywatersprayquenchinginapress.Theeffectofpresspressure,water

sprayingtime,watersprayingpressureandquenchingwatertemperatureonlengthincrementoftheshovelingblades

wasinvestigated.Theresultsindicatethatthesequenchingprocessparameters,particularlypresspressure,will

exertanappreciableinfluenceonthelengthincrementoftheshovelingbladesexceptwatersprayingtimeKeywords:shovelingblade;heattreatment;expansioncoefficient

随着我国经济的快速发展，工程机械零部件市场逐渐升温，为业内人士普遍看好。目前，我国工程机械零部件正在从低水平、低质量、低价位、满足功能型向高水平、高质量、中价位、经济实用型过渡。铲刃是工程机械的高消耗配件，其生产的工艺流程为：下料-钻孔-冲孔-热处理-表面清理-包装。铲刃的综合力学性能、互换性、使用寿命等主要决定于它的热处理质量。而热处理的难点是膨胀系数的确定。只有确定了膨胀系数才能确定机加工下料尺寸，钻孔、冲孔的孔距。为此对铲刃作了大量的热处理试验工作，寻找合理的工艺参数，得到了一些有益的启示。

1产品简介

铲刃主要用作平地机配件。平地机主要功能为利用铲刃平整地面的土方机械，适用于构筑路基和路面、修筑边坡、开挖边沟，也可搅拌路面混合料、扫除积雪、推送散粒物料以及进行土路和碎石路的养护。因平地机的型号不同，铲刃的规格有上百种。其主要技术要求为高强度、高韧性、高耐磨性、高互

换性。现阶段，铲刃的高强度、高韧性、高耐磨性均能通过热处理得到保证，但高互换性因其膨胀的不确定性而不能有效保证。

本文所述铲刃长600～2500mm,宽152~203mm,厚12～25mm,为弧形，如图1所示。材料为25CrMnB钢。热处理要求：表面硬度44~52HRC,心部硬度大于42HRC,热处理后长度的膨胀量变化小于2mm。

图1铲刃简图

Fig.1Schematicdrawingoftheshovelingblade

2热处理

2.1设备

所使用的热处理生产线是北京机电研究所制造的铲刃专用生产线，由上料辊道、辊底式天然气加热炉、快速出炉辊道、淬火系统(含供水及水循环系

收稿日期：2014-08-20

作者简介：刘强(1967-),男，重庆人，工程师。联系电话·42·