HTPB基聚氨酯溶胀实验与机理研究

：通过HTPB聚氨酯的溶胀实验，比较不同溶剂对其的溶胀效果。实验结果表明，

不同溶剂对HTPB聚氨酯的溶胀效果差异较大，三氯甲烷对HTPB聚氨酯的溶胀率最高，

可达到700%以上.选取的七种溶剂溶胀率的排序为三氯甲烷甲苯二氯甲烷苯环己烷

乙酸乙酯。针对三氯甲烷讨论了温度对溶胀度的影响，结果表明温度对溶胀率没有明

显的影响，仅仅缩短了溶胀平衡所需的时间。分子动力学模拟计算了溶剂与HTPB聚氨酯

的结合能以及溶剂在其中的扩散系数，模拟结果与实验值顺序相吻合。

：HTPB聚氨酯；溶胀率；溶剂；温度

:TheswellingeffectofdifferentsolventsontheHTPBpolyurethanewascompared

throughtheexperiments.Resultsshowsthattheswellingeffectvariesconsiderablywithdifferent

solvents.Inthecommonsolvents,trichloromethanehadabestswellingrateofHTPBpolyurethane

whichwasmorethan700%.Theswellingratesofthesevensolventsusedintheexperimentwerein

followorder,trichloromethanemethylbenzenedichloromethanebenzenecyclohexaneethyl

acetateacetone.Thetemperaturehadnoobviouseffectofswellingrate,itonlyshortenthetimeto

reachequilibrium,thetimewas270minat25℃,240at35℃and180minat45℃.Thediffusion

coefficientofthesolventintheHTPBpolyurethanewascalculatedbymoleculardynamics

simulationandtheresultswereinagreementwiththeexperimentalresults.

Keywords：HTPBpolyurethane;swellingrate;solvents;temperature

1.引言

丁羟复合固进剂(HTPB推进剂)是一种成推进剂，具有粘度低、工艺与力学性

能好、可容纳较高的固体含量以及燃速调节范围宽等优点，是目前主要研究和应用较广泛的

[1,2]

推进剂体系。推进剂具有一定的使用，到达的推进剂会发生老化和化学老

[3]

化，进而影响的稳定性和安全性。

对于废弃推进剂组分的回收，药柱是提高组分回收率的主要途径之一。由于HTPB

[4]

聚氨酯具有很高的交联度，在溶剂中无法溶解，且其具有良好的力学性能性能，HTPB-IPDI

[5]

体系的力学性能良好，断裂伸长率能够达到950%以上，中会严重的发热，增加

[6,7]

了药柱的不安全性。

溶胀后的药柱虽然仍保持固态，但强度和断裂伸长率急剧下降，因此研究HTPB基聚

氨酯的溶胀对浇铸的回收具有很大的意义。本文选取了七种不同溶剂对HTPB基聚氨

酯进行了溶胀，分别比较了其溶胀效果，选取溶胀效果好的溶剂，进而比较不同温度对溶胀

效果的影响。

[8,9]