回收精炼液态渣在转炉出钢渣洗的实践.pdfVIP

回收精炼液态渣在转炉出钢渣洗的实践 唐利民 丁金虎 解林冲 周 禹 何航 杨 建 1 （湖南华菱湘潭钢铁公司，湘潭 411101 ） 摘 要 本文介绍了湘潭钢铁集团公司五米宽厚板厂回收液态精炼渣的渣洗工艺实践，该工艺不影响精炼渣终渣成 分，而且回收渣渣洗工艺能保证较佳的脱硫效果，并且有助于 LF 炉快速成渣；同时该工艺可以降低钢中气体含量。 另一方面这种工艺可以降低原材料的消耗和能耗，平均降低生产成本约 10.84 元/t 。 关键词 渣洗 精炼渣 循环应用 脱硫 Slag Infiltration Practice by Recovery Refining Hot Slag in BOF Tapping Tang Liming Ding Jinhu Xie Linchong Zhou Yu He Hang Yang Jian （Xiangtan Iron and Steel Co., Ltd., Xiangtan, 411101 ） Abstract This article introduces the process practice on the re-utilization of LF hot refining slag infiltration on BOF tapping in the Five-Meters Wide Heavy Mill Plant of Xiangtan Iron ＆ Steel Group Co.. The process not only can’t affect the final refining slag composition but also can ensure better effect of desulfurization and benefit of white slag forming. At the same time this process can reduce gas content in the steel. On the other hand this process can reduce the cost of raw material and energy consumption. The average production cost is reduced by 10.84yuan/t. Key words slag infiltration; refining slag; re-utilization; desulfurization 1 引言 20 世纪 90 年代国外已有精炼渣的回收利用的相关报道[ 1,2],最近几年由于生产成本的压力及环保的 需要，国内很多钢厂也在回收利用精炼渣方面做了大量工作，有的钢厂直接回收连铸后的 LF 炉渣倒入 LF 炉的冶炼前期[3]，有较好的冶金效果。湘钢铁水硫含量不高，在精炼后渣仍有较好的脱硫能力，湘钢从 2004 年开始也采用这种模式回收精炼渣，从 2010 年开始，湘钢五米宽厚板厂开始试验直接回收连铸后的 精炼渣在转炉出钢进行渣洗的工艺，经过试验后目前已经形成了成熟的回收渣的渣洗工艺，精炼渣的回收 比例约为40% 。 2 工艺流程和渣洗工艺简介 湘钢五米宽厚板厂主要产品为宽厚板，目前炼钢主要设备为：120t 转炉 2 座、120t LF 双工位钢包炉 3 座、120t VD 双工位真空脱气装置一套，120tRH 双工位真空脱气装置一套，直结晶器连续弯曲连续矫直弧 形板坯连铸机两台，转炉出钢量为 135～145t。生产中有三条工艺路线即分三种，一是BOF→LF→VD→CC， 其次是 BOF→LF→RH→CC，最后是BOF→LF→CC 。由于生产节奏的问题和为了保证脱硫效果一般精炼渣 的回收不超过两次。 唐利民，男，硕士，湘钢五米宽厚板厂，工程师，从事炼钢技术工作。 回收精炼液态渣在转炉出钢渣洗的实践