离子液体法制备铜的纳米粒子.pdfVIP

离子液体法制备铜的纳米粒子/王辰光等 ·31· 离子液体法制备铜的纳米粒子 王辰光，赵荣祥，徐铸德，马 琳 (浙江大学化学系物理化学研究所，杭州 310027) 摘要 利用化学还原方法，加入不同量的离子液体 1-甲基-3-乙基咪唑硫酸乙酯盐，制备了不同大小的金属铜的纳米 粒子。采用 X 射线衍射和透射电子显微镜对所制备的样品进行了结构表征。结果表明，两个样品中的粒子都具有五边形和 六边形结构，粒径约为 200~300nm ，离子液体不但作为分散剂影响粒子的大小，而且有一定的防氧化作用。 关键词 铜纳米粒子 室温离子液体 X 射线衍射 透射电子显微镜 Preparation of Copper Nanoparticles in Room Temperature Ionic Liquid WANG Chenguang,ZHAO Rongxiang,XU Zhude,MA Lin (Physical Chemistry Research Institute, Department of Chemistry, Zhejiang University, HangZhou 310027) Abstract Copper nanoparticles are synthesized in the room temperature ionic liquid with different contents via chemical reduction under the same ambient conditions. X-ray power diffraction and transmission electron microscopy are used to characterize the structure of the Cu nanoparticles. The results indicate that the mean diameter of the nanoparticles is about 200nm~300nm. It is concluded that the ionic liquid is not only used as dispersant which influences the diameter of the nanoparticles but also as stabilizing agent to prevent the oxidation of copper nanoparticles. Key words Cu nanoparticles, room temperature ionic liquid, X-ray diffraction, transmission electrons microscopy 0 前言 1.2 铜纳米粒子的制备 离子液体的全称是室温离子液体，即在室温或室温附近 配制 0.2mol/L 的CuSO4 溶液，记为 A; 0.3 mol/L 的抗坏 呈液态的由离子构成的物质。由含氮、磷的有机阳离子和大 血酸溶液，记为 B ；6.0 mol/L 的 NaOH 溶液；室温下，用 的无机阴离子组成，有着不同于水溶液及普通有机溶剂的诸 NaOH 溶液调节 10ml B 的pH 值达到 12.0，然后加入 3ml 离 多性质，如较高的热稳定性和化学稳定性，极低的蒸气压， 子液体，将此混合溶液记为 C 。将C 水浴加热至 80℃，搅拌 良好的导电性，较大的电化学窗口，强极性以及溶解各种有 下将 10ml A 滴加入 C 中，加完后继续搅拌 20min ，得棕红 [1] 机、无机材