聚乙烯醇-海藻酸钙制备的研究及优化.pdfVIP

聚乙烯醇-海藻酸钙制备的研究及优化/王孝华 ·31 · 聚乙烯醇-海藻酸钙制备的研究及优化﹡ 王孝华 (重庆交通大学理学院，重庆 400074) 摘要 本实验首先以含水率为指标，探讨了戊二醛用量、聚乙烯醇与海藻酸钠的质量比、CaCl2 浓度、戊二醛与聚乙烯 醇的反应时间等因素对聚乙烯醇-海藻酸钙复合材料的影响，结果表明，当戊二醛的含量为 0.85%、聚乙烯醇在材料中比例 增大到8 ︰1 左右、CaCl2 溶液质量分数达2% 、戊二醛与聚乙烯醇的反应时间为1.5h 时，复合材料的含水率最高。然后通过 正交实验设计，对聚乙烯醇-海藻酸钙聚合物制备的条件进行优化，找出最佳的制备条件：ω(戊二醛)为 0.85%、m(PVA) ︰ m(NaAlg)为8 ︰1、ω(CaCl )为2.0% 。 2 关键词 聚乙烯醇-海藻酸钙 制备 优化 最佳条件 中图分类号：O647.33 文献标识码：A Research and Option in the Preparation of PVA-alginate-Ca WANG Xiaohua (School of Science, Chongqing Jiaotong University, Chongqing 400074) Abstract Based on water content, the influence of different glutaraldehyde contents, different ratios of m(PVA):m （NaAlg ）, different CaCl2 contents and different reaction times between glutaraldehyde and PVA on PVA-alginate-Ca was studied, The results show that the water content is the highest when glutaraldehyde content being 0.85%, the ratio of m(PVA) ︰m(NaAlg)being 8 ︰1, CaCl2 concentration being 2% and the reaction time being 1.5h. The preparation condition of PVA-alginate-Ca was optimized by experiment. The optimum preparation conditions were selected, the glutaraldehyde concentration 0.85%, the ratio between PVA and NaAlg being 8 ︰1 and CaCl concentration 2.0%. 2 Key words PVA-alginate-Ca, preparation, option, optimum conditions 拌下滴加戊二醛溶液，用盐酸调节 pH=6.5 ，在室温下反应 0 引言 0.5h （溶液粘度增大，戊二醛与聚乙烯醇发生交联反应），滴 海藻酸钠的分子链上含有大量的羟基和羧基，用氯化钙 加一定量的海藻酸钠（NaAlg ）溶液，继续搅拌 0.5h ，除去 溶液（CaCl2 ）作为交联剂，可形成交联的海藻酸钙聚合物， 气泡，倒入表面皿中，置于35℃烘箱中烘干成膜，取出；加 含水率高，具有好的良好的生物降解性和生物相容性，可用 入 100mL 质量分数为2%CaCl2 溶液，浸泡4h ，膜材料由透 于食品加工、制药。聚乙烯醇（PVA ）无毒性，其分子链上