高韧性钢丸的微合金化及等温淬火工艺研究.pdfVIP

铸 造 Dec. 2009 1256 FOUNDRY Vol .58 No.12 · · 高韧性钢丸的微合金化及等温淬火工艺研究 杨思一 （山东理工大学机械工程学院，山东淄博255049） 摘要：分析了目前钢丸的使用情况和不足。通过微合金化和等温淬火工艺，研究一种新型高韧性钢丸。确定了合适的 化学成分范围，获得正确的淬火工艺参数，得到以下贝氏体为主的淬火混合组织。在保证钢丸足够硬度的基础上，提 高了钢丸韧性，保证了钢丸的清理效果，延长了使用寿命。 关键词：钢丸；微合金化；等温淬火；贝氏体；韧性 中图分类号： 文献标识码： 文章编号： TG142.72 A 1001-4977 （2009）12-1256-04 Study on Micro-Alloying and Isothermal Quench of Steel Shots with High Toughness YANG Si-yi （School of Mechanical Engineering, Shandong University of Technology, Zibo 255049, Shandong, China） Abstract ：Application status and disadvantage of exiting steel shot were analyzed. By micro-alloying and isothermal quench a new kind of steel shot with high toughness was developed. Through confirming the appropriate chemical composition of the steel and quenching parameters, the bainite structure was obtained. On the basis of assuring its hardness, the steel shot with improved toughness, better cleaning effect and prolonged service life is gained. Key words ：steel shot; micro-alloying; isothermal quench; bainite; toughness 早期金属磨料的材质是白口铸铁，白口铸铁硬度 的，获得高韧性钢丸。选择合适的淬火介质，确保奥 高，但是由于脆性大，易破碎，已经不能适应现代工 氏体的转变温度和保温时间。借助于显微镜，观察钢 业的要求，基本被淘汰。国外从19 世纪50 年代发展 丸的金相组织，分析下贝氏体的含量与分布。测试分 了第二代金属磨料高碳钢丸，在金属表面清理、除锈 析等温淬火钢丸的力学性能，主要包括钢丸的韧性和 和金属强化等方面，迅速取代了传统的白口铸铁钢丸。 耐磨性，并与高碳钢丸进行比较。 国内高碳钢丸的研究始于 19 世纪80 年代，根据 1 研究过程 国家标准GB 6484—86 和GB 6485—86 的规定，普通 钢丸的化学成分：0.85%~1.20% C，0.40%~1.50% Si， 钢丸的生产工艺流程：熔炼造粒→粗分→淬火→ 0.60%~1.20% Mn，P ≤0.05%，S≤