真空燒結法對鈦銅鉬合金添加碳化鉭之顯微組織與強化機制探討.pdfVIP

真空燒結法對鈦銅鉬合金添加碳化鉭之顯 微組織與強化機制探討 Effects of Vacuum Sintering Process on t he Microstruct ure and Strengthening Mechanisms of Tantalum Carbides Added Ti-Cu-Mo Alloys 1 2 3 4 1 2 3 4 S.H. Chang , J.R. Huang , C.C. Lin , C. Liang 200 Titanium alloys have been developed and applied in last 200 years. They have excellent physical properties, corrosion resistance and biocompatibility suitable for aerospace and biomedical applications. Powder metallurgy (P/M) of titanium and its alloys often have lower relative den sity and strength than that from other processes. It is important to develop a new powder metallurgy process that will improve the P/M of titanium alloy properties. (Ti-12Cu-8Mo) In this study, three different powders were prepared and vacuum sintered to produce the optimal Ti-Cu - Mo alloy s (Ti- 12Cu -8Mo) . In order to improve th e Ti- microstructure and properties of sintered Ti-Cu-Mo alloys, 12Cu-8Mo 1200 all of the optimally sintered specimens were alloyed 5 wt% (TaC) with TaC. Experimental results showed that after 1200 (98%) (43.89 HRC) vacuum sintering and adding 5 wt% TaC carbide, the (1040 MPa) alloys have higher density (98%), hardness (43.89 HRC) and transverse rupture strength ( 1040 MPa). However, 5 wt% TaC the influence of grain boundary defects weakened the (Ti-12Cu-8Mo) corrosion resistance of Ti-12Cu-8Mo alloys. 關鍵詞： Key words: Pow der m et allurgy, Ti-Cu -Mo alloy s,