C／SiC-（W-C）复合材料的制备及烧蚀性能.pdfVIP

维普资讯 第26卷 第1期 材 料 科 学 与 工 程 学 报 总第111期 Vo1．26 No．1 JournalofMaterialsScience Engineering Feb．2008 ArticleID：1673-2812(2008)01-0012·04 ProcessingandAblationPropertiesofC／SiC一(W—C)Composites TONG Chang-qing，CHENG Lai—fei，ZHANG Li—tong，XU Yong-dong (NationalKeyLab．ofThermostructureCompositeMaterials，Northw~ternPolytechnicalUniversity，Xiall 710072，China) [Abstract] A 3DC／SiC一(w—C)compositewaspreparedbycombiningchemicalvaporinfiltration(CVI)technologywith solution impregnationmethod．Thephasecompositionandm icrostructureofthecompositebeforeand afterablationwere investigatedbyXRD，andSEM ，respectively．Theablationpropertiesofas—preparedC／SiC-(W—C)compositewerestudied ． TheXRD resultsshow thatthemainphasesoftheas—preparedcompositeareWC，W ，SiC andC whilethoseoftheablated surfaceareW O3，W andSiC．SEM analysisimpliesthatnotonly inter-bundleporesbutalso intra-bundleporesarefilledby W—C．Theas-preparedc／sic一(W—C)compositeattainsadensityof3．3g／cm。withtheapparentporosityof11 ．Itslinear andmassablationratesare4．3X10 mm／sand7．2×10 。g／s，respectively． [Keywordsl ablation；CVI；solutionimpregnation；C／SiC～(W～C)composite CLC nllmbe ：V257；T13333 DocumentCode：A C／SiC-(W-C)复合材料的制备及烧蚀性能 童长青 。成来飞 。张立同。徐永东 (西北工业大学超高温结构复合材料 国防科技重点实验室 ．陕西 西安 710072) 【摘 要】 采用化学气相渗透 (CVI)结合溶液浸溃法制备 3I)_c／sic一(w—c)多元基复合材料，利用 XRD、SEM 技术对材料烧蚀前后 的物相组成及微观结构进行表征，并讨论 了复合材料 的烧蚀性能。结果表 明，3D-C／SiC一(W— c)复合材料 的主要成分为WC、W 、SiC和 c，而烧蚀表面的主要成分为 WO。、W 和 SiC。W—C不