双组分水性塑塑复合胶的研究 陈小锋沈峰 (北京高盟新材料股份有限公司北京102502) 要原料合成了水性丙烯酸乳液，加入固化剂，得到双组分水性丙烯酸复合胶。研 究了软／硬单体比例、功能单体用量、乳化剂用量以及固化剂对产品性能的影响。 实验结果表明，当软／硬单体质量比为1．5、功能单体占单体总量的5％，固化剂 用量为1．0％，所得的双组分水性丙烯酸复合胶的性能较佳。 关键词。水性丙烯酸；双组分；干法复合；剥离强度 on water-basedadhesivefor films Study acrylic two-component laminatingplastic Chen Shen Xiao—feng Feng ComensNewMaterials 1 02502China) (Beijing Co．Ltd，Beijing Abstract：TheemulsionWas with acidand acrylic synthesizedbutylacrylate，styrene，acrylic raWmaterials．Thenthe water-based hydroxylethylacrylate弱main two-componentacrylic adhesivefor filmsWas theemulsionandwater-based laminatingplastic preparedusing curing ofso．hard monomer monomer contentand agent．Effects ratio，functionalcontent，emulsifier onthe ofemulsionadhesivewere results showedthat curingagent properties investigated．The whenthesoft／hardmonomerratiois functionalmonomercontentis emulsifier I．5，the 5％，the contentis3％and contentis1．0％．the oftheadhesiveisbeaer． curingagent property words：water-based Key acrylicemulsion；two-component；dry·typelamination；peelingstrength． 前言 随着人们环保意识的提高和各项环保立法的加强，应用在食品和医药领域的 溶剂型软包装用胶粘剂将会越来越受到限制，而水性胶粘剂将得到广泛应用。水 性丙烯酸酯胶粘剂具有独特的耐气候性、耐老化性、抗氧化性、断裂伸长率高、 耐水性好等一系列优点，加之其制备工艺简单，产品类型丰富多样，价格较廉， 性能稳定，已成为国内外研究的热点n圳。 然而，单一的丙烯酸酯类单体所制备的水性胶粘剂并不能达到理想的粘接效 果，需要对