可生物降解聚合物同时作为生物膜载体和反硝化碳源去除污水中氮的研究.pdfVIP

可生物降解聚合物同时作为生物膜载体和反硝化碳源去除 污水中氮的研究* 初里冰，王建龙 （清华大学核研院环境技术研究室，北京 100084 ） 摘要：本论文研究采用以可生物降解聚合物PCL 为生物膜载体和碳源，同时硝化反硝化去除低碳氮比废水 中的有机物和氮。结果表明在水力停留时间为18 h，TN 的去除率可以达到75% 。去除每克氮消耗的PCL -1 量为1.27 ± 0.09 g PCL g N 。 关键词：可生物降解聚合物；生物膜；同时硝化反硝化 中图分类号：TQ 028.8 文献标识码：A Nitrogen removal using biodegradable polymers as carbon source and biofilm carriers in a moving bed biofilm reactor Libing Chu ，Jianlong Wang (Laboratory of Environmental Technology, INET, Tsinghua University, Beijing 100084, China;) Abstract ：In this paper, biodegradable polymer (PCL) was served as both solid carbon source and biofilm carriers to remove nitrogen from wastewater with a low C/N ratio by simultaneous nitrification and denitrification (SND) in a moving bed biofilm reactor. The results showed that the average TN removal efficiency was 75% at hydraulic retention time of 18.5 h. PCL was available both for microbial attachment and for carbon source. The consumed PCL amount for removing per -1 gram of TN was calculated to be 1.27 g PCL g N. Key words ：Biodegradable polymers ；biofilm ；simultaneous nitrification and denitrification 引 言 生物脱氮是目前处理氮污染的主要手段。随着污水处理标准的提高，对总氮的排放标准 日趋严格。我国现行的污水处理工艺普遍存在因脱氮碳源不足而影响脱氮效率的问题，深入 研究外加碳源的利用机制、开发有效的生物脱氮新工艺，已经成为污水处理领域急需解决的 关键问题。 本论文研究采用可生物降解聚合物作为生物膜的载体和固体碳源，同时硝化反硝化去除 污水中氮。拟处理的废水为低碳氮比的废水，采用的反应器形式为生物移动床。目前，固体 碳源主要应用在厌氧反硝化去除饮用水和地下水中的硝酸氮[1-3]，在污水处理中的应用还鲜 有报道。 1 实验材料和方法 1.1 反应器和进水组成 图1 为生物移动床反应器的示意图。反应器由有机玻璃做成，分为6 L 的曝气区和3.5 L 的沉淀区。可生物降解聚合物PCL 载体的填充率为11.3% (V/V)。 PCL 比表面积为 0.376 m2 -1 -1 -1 g ，密度为 1.12 kg L 。反应器底部装有曝气头，曝气流量通过流量计控制在80-100 L h 。 反应器内溶解氧浓度保持在 2.75-3.67 mg/L. 温度通过水浴夹层控制在30