第38卷 第6期 人 工 晶 体 学 报 V01．38 No．6 2009年 12月 JOURNAL OF SYNTHETIC CRYSTALS December，2009 PhotocatalyticPropertiesofSi-d·oped TiO2byHydrothermalM ethod LIUYan—min，ZHANGXue-jing， Jing．ze，ZHANGYan-feng ，WEIYu (1．CollegeofChemist~andMaterialScience，HebeiNormalUniversity，Shijiazhuang050016，China； 2．CollegeofLifeScience，HebeiNomralUniversity，Shijiazhuang050016，China) (Received20july2008) Abstract：A seriesofSi—dopednanocrystalline titaniapowderswerepreparedbyhydrothermalmethod usingtitaniumtetrachloride(TiC14)andsodium silicate(Na2SiO3)asprecursors．Thephotocatalysts werecharacterizedbyX—raydiffraction(XRD)analysis，fouriertransform infraredspectroscopy(FI一 IR)，UV．visdiffusereflectancespectrophotometer(UV—visDRS)．AstheSidoped，photocatalystswith smallercrystalsize．highercontentofanatasephasewereobtained．ItwasalsofoundthatTi-O—Siband wasfomr edintheSi—dopedsamples．ThephotocatalyticactivityofSi—dopedTiO2wereimprovedcompare withnon—doped．ThepossiblereasonsofSi—dopedfortheenhancedphotocatalyticactivitywasdiscussed． Keywords：Si-doped；TiO2；hydrothermalmethod；photocatalyticactivity CLCnumber：0643 Documentcode：A ArticleID：1000-985X(2009)06．1399-05 水热法制备硅掺杂纳米TiO：的光催化性能 刘艳敏 ，张雪景 ，刘敬泽 ，张艳峰 ，魏 雨 (1．河北师范大学化学与材料科学学院，石家庄 050016；2．河北师范大学生命科学学院，石家庄 050016) 摘要：以TiC1和Na2SiO，为原料，采用水热法制备 了一系列掺杂 si的纳米TiO：粉体。采用 x射线衍射分析 (XRD)，红外光谱(fTr—IR)，紫外可见吸收光谱 (uV—visDRS)对样品进行了表征。结果表明：掺杂si的TiO：样品粒 径较小，样品中锐钛矿的百分含量有了一定提高。同时发现在 si掺杂的样品中有 Ti-O-Si键的存在。掺杂 si的 TiO样品的光催化活性较未掺杂样品有了较大提高。并讨论了Si掺杂提高 TiO 光催化活性可能的原因。 关键词 ：si掺杂；TiO：；水热法 ；光催化活性 1 Introduction TiO2co