聚氨酯共混膜的制备工艺条件研究论文.pdfVIP

B038 聚氨酯共混膜的制备工艺条件研究 李婧娴 董声雄 曾振辉 （福州大学化学化工学院， 福州 福建 350002） 摘 要 利用 L-S 相转化法将聚醚型聚氨酯（PEU ）和聚醚砜（PES ）共混，以聚乙二醇（PEG ）为添加 剂，制备 PEU 共混膜。通过测定比较共混膜的结构与性能，结果表明：聚合物浓度、共混组成比、添加剂 种类与浓度是影响 PEU/PES 共混膜性能的主要因素。 关键词 聚氨酯 聚醚砜 共混膜 制备工艺条件 中图分类号 TQ 028.8 文献识别码 A STUDY ON PREPARATION TECHNOLOGY OF POLYURETHANE BLEND MEMBRANES LI Jingxian, DONG Shengxiong and ZENG Zhenhui (College of Chemistry and Chemical Engineering, Fuzhou University, Fuzhou 350002, Fujian, China) Abstract Polyether-polyurethane (PEU) and polyethersulfone (PES) were blended for preparing PEU blend membranes by using L-S phase-inversion method in the presence of polyethylene glycol as addictive. By measuring and comparing structures and performances of different blend membranes, the results showed that polymer concentration, blend composition, the kind and the concentration of addictive were the main influence factors to PEU blend membrane performances Keywords polyurethane ，polyethersulfone ，blend membrane ，preparation technology 引 言 最近几年一大批专家学者致力于开发能响应各种环境变化的新型膜 [1,2] 。选择具有形状 记忆功能的膜材料和对聚合物膜材料进行共混改性，可用来制备 pH 敏感膜的基膜材料。应 用于生物医学、药物释放系统（DDS ）、制药等领域的膜材料之一——聚氨酯（PU ），以其 独特的化学结构使其具有优异的抗拉性、生物相容性和耐超低温性，被美国列为今后重点发 展的三大生物医用高分子材料之一[3] 。但只用纯聚氨酯制备出的膜是无孔膜，且机械强度不 够高，作为 pH 敏感膜的基底膜还存在缺陷。共混法能将几种性质不同而相容性较好的成分 结合在一起，综合均衡不同材料的性能，克服单一组分的不足，使制备兼有多种聚合物特性 的膜成为可能。如 Sivakumar 等用醋酸纤维素（CA ）与PU 共混制膜[4] ；封严用PU 分别与 [5] CA、聚丙烯腈（PAN ）、聚砜（PS ）制得共混膜 ；Malasamiy 等用磺化聚砜（SPSF）与PU 共混，从而在一定程度上改善了膜性能[6] 。因为聚醚砜是很好的生物医学用的膜材料，所以 本文研究聚氨酯与聚醚砜共混膜的制备工艺条件。通过聚合物之间相容性的差异来调节共混 膜结构，提高膜的水通量和截留率，改善膜的亲水性和机械性，得到一种综合性能较好的共 联系人：董声雄。第一作者