高频燃烧红外吸收法测定硅铁中的碳硫 ·1 · 高频燃烧红外吸收法测定硅铁中的碳硫 郭飞飞 （中国钢研科技集团有限公司钢研纳克检测技术有限公司, 北京 100081 ） 摘 要 本文采用高频燃烧红外吸收法测定硅铁中的碳硫，对称样量、助熔剂、峰形、飞溅、熔体等做了对比实验， 得出最佳分析条件是 0.15g 硅铁样品+0.6gFe+1.8gWSn 。并分析了多个样品的精度和准确度，结果表明 RSD_C%=0.49%~2.1% ，RSD_S%=1.9%~3.9% 。 关键词 高频燃烧 红外吸收法 硅铁 碳硫 Determination of Carbon and Sulfur in Ferrosilicon by High Frequency Combustion-infrared Absorption Method Guo Feifei (China Iron and Steel Research Institute Group Co., Ltd., NCS Testing Technology Co., Ltd., Beijing, 100081) Abstract By contrasting the sample weight, flux, peak shape, splash and melt, carbon and sulfur of ferrosillicon samples were analysed by high-frequency combustion infrared absorption method. The best method was 0.15g sample +0.6g Fe +1.8g WSn. And precision and accuracy of some sample were analysed, the result was RSD_C%=0.49-2.1%, RSD_S%=1.9-3.9%. Key words high-frequency combustion, infrared absorption method, ferrosilicon, carbon and sulfur 硅铁作为合金元素加入剂，广泛用于低合金结构钢、合金钢、弹簧钢、轴承钢、耐热钢及电工硅钢之中。 硅铁中碳的含量一般不超过 0.20%，硫的含量一般不超过 0.020%[1] 。目前硅铁中碳的测定采用国标 GBT 4333.10—1990 硅铁化学分析方法 红外线吸收法测定碳量[2]，但实验步骤较多，硅铁中硫含量的测定采用国标 GBT 4333.7—1984 硅铁化学分析方法 色层分离硫酸钡重量法测定硫量[3]，操作繁琐，精度低且测定下限偏高。 本文采用钢研纳克公司生产的 CS-3000 高频红外碳硫仪测定硅铁中的碳硫含量，具有高频燃烧能量充 分，分析流量稳定，红外检测出限低、线性好的优点，通过试验选择最佳的分析条件，对硅铁中的碳硫含量 进行测定，获得令人满意的结果。 1 实验部分 1.1 主要仪器、材料及试剂 CS-3000 高频红外碳硫分析仪（钢研纳克检测技术有限公司）；电子天平(灵敏度为0.1 mg)；马弗炉： 国家科技部创新方法工作专项项目(2011M060500) 。 郭飞飞, 女, 硕士, 助理工程师, 主要从事化学分析, guofeifei@ ·2 · 第九届中国钢铁年会论文集 额定温度为1300℃。助熔剂：钨（w （C ）≤0.000 8%,w （S）≤0.000 5% ），锡（w （C ）≤0.000 8%,w