低铋环保型无铅釉上彩熔剂研究.pdfVIP

低铋环保型无铅釉上彩熔剂的研究 王秀文 刘大成 朱晓丽 董秀珍 陈瑞军 刘臻 丛丽娜 （唐山学院环境与化学工程系 唐山 063000 ） 摘 要：以碱-硼-硅系统熔剂为基础，用多种碱金属、碱土金属及外加剂的复合作用来代替铅 在熔剂中的作用，研制了熔融性能好、化学稳定性好、彩烤效果好的低铋环保型无铅釉上彩熔剂。 试验结果表明：Li O:Na O:K O为0.65:1:0.33，CaO:MgO:SrO:BaO比在（0.31～0.33）：1：0.33：（0.27～ 2 2 2 0.34），外加剂氧化铋、氧化镧、氧化钼、氧化钨的外加量分别控制在 5%、1%、1.25%、1%时熔剂 性能最佳。 关键词：低铋 无铅 釉上彩 熔剂 Study on Environment-Fridenly Leadless Flux for Overglaze Colors with Low Bismuth Content Wang Xiuwen,Liu Dacheng,Zhu Xiaoli,Dong Xiuzhen,Chen Ruijun,Liu Zhen,Cong Lina (Department of Environmental and Chemical Engineering, Tangshan College, Tangshan 063000) Abstract:Based on alkali-boron-silicon system, a compound function of several alkali metals, alkaline-earth metals and admixtures is used to replace that of lead to develop environment-friendly,leadless flux for overglaze colors with low bismuth content. Li O:Na O:K O as well as CaO:MgO:SrO:BaO and the addition quantities of Bi O , La O , MoO , 2 2 2 2 3 2 3 3 WO3 were studied.Considering the fusion property, chemical stability and decoration firing effect,an optimum condition is obtained. Key words:low bismuth,leadless,overglaze colors,fluxs 1 前言 降低陶瓷装饰材料中的铅、镉溶出量，一直是困惑陶瓷行业的老课题与大难题。近些年，国内 外的学者一直致力于无铅无镉釉上彩熔剂的研究开发工作，并取得了一定的成果。如周大俊等人通 过对无铅无镉颜料机理的研究，用含有多种氧化物的熔剂取代了釉上颜料中的氧化铅，研制出了达 到 ZBY24007—89 的无铅颜料，并用于网印陶瓷釉上花纸的生产[1]。曹春蛾等人以碱-硼-硅系为基础 加入了锶-氟助熔助色剂研制了适应红色色剂的无铅无镉熔剂[2]。山东省硅酸盐研究设计院的殷书建 等人用透射和扫描电子显微镜及 X-射线能谱仪研究了无铅无镉熔剂的显微结构与化学稳定性的关 系，分析了影响熔剂化学稳定性及热膨胀性能的各种因素。探讨了各种不同熔剂对颜料呈色性能的 影响，较好的解决了无铅无镉颜料的技术难题[3]。曹春蛾等人对已有文献中关于降低陶瓷炊餐具铅、 镉溶出量进行了归纳，叙述了无铅、无镉陶瓷炊餐具装饰材料用釉料、颜料的研究进展，并提出了 今后陶瓷炊餐具装饰材料的发展方向[4]。王迎军等对掺铈新型氧化物系统无公害釉上颜料用熔剂进 行了深入研究[5]，无铅无镉釉上彩熔剂研究取得重大进展。 国外在这方面的研究也有很大的突破。美国已发明专利--无铅无镉低温搪瓷釉块，这一发明对 与食品接触的搪瓷釉块的生产有很大的帮助[6]。日本学者用含氧化镧的硼酸盐玻璃制成了一些新的 无铅熔块并对这类熔块的晶化倾向、