氟掺氧化锡(SnO2%3aF)纳米粉末制备.pdfVIP

B54 氟掺氧化锡（SnO :F）纳米粉末的制备 2 侯宝峰，刘孝宁，孙本双 (西北稀有金属材料研究院，国家钽铌特种金属材料工程技术研究中心，宁夏 石嘴山市 753000) 摘要：本文以 SnCl 、氨水和 HF 酸为主要原料，用化学方法制取了氟掺氧化锡纳米粉末。用 XRD 、SEM 4 分别研究了 FTO 粉末的相组成和粉末形貌，用比表面仪测定了粉末比表面积，同时测试了 FTO 粉末的压 粉电阻。研究表明：氟掺氧化锡粉末仍是正四面体金红石结构，500℃下焙烧出的粉末导电性最好，合适的 焙烧温度、无水酒精球磨分散和分散前控制先驱体干胶中水分含量是制取纳米 FTO 粉的关键。 关键词：透明导电氧化物；氟掺氧化锡；球磨分散；粉末电阻 中图分类号：TF123.7+2；TB34 文献标识码：A 文章编号： Preparation of Fluorine-doped Tin Oxide (SnO :F) Nano-powder 2 HOU Baofeng, LIU Xiaoning, SUN Benshuang (Northwest Rare Metal Materials Research Institute, Shizuishan 753000, Ningxia, China) Abstract: Fluorine-doped tin oxide (SnO :F) nano-powder were prepared by chemical methods. The phase 2 composition and the morphology of FTO powder were studied with XRD and SEM, the specific surface area and the resistance of the FTO powder were measured. The results showed that, fluorine-doped tin oxide powder was the rutile structure, the powder calcined at 500 ℃ had the best conductivity, and the powder particle size was influenced by the calcination temperature, ball-milling in anhydrous alcohol and the moisture content of precursor before calcined. Key words: transparent conductive oxide; fluorine-doped tin oxide; ball milling dispersion; powder resistance 前言 透明导电氧化物（TCO: Transparent Conductive Oxide ）是功能材料中比较特殊的一类材料，其中研究 最多的是 ITO （In O :Sn）、FTO(SnO :F）、ZAO(ZnO:Al)及 ATO(SnO :Sb)等。相比较其它的透明导电材料， 2 3 2 2 氟掺氧化锡（FTO ）具有具有低成本、高导电性、可见光区高透光率、热稳定性和化学稳定性好、硬度高 120 等优点，因此，FTO 从一开始就受到广泛的关注和研究。 氟掺氧化锡材料（SnO :F）是在二十世纪四十年代开始生产的，起初应用于飞机驾驶窗玻璃，经过