腐蚀和摩擦交互作用对人工关节钴合金材料损失机理的影响.pdfVIP

The 6th China Corrosion Conference Effect of Bio-Tribo-Corrosion Interactions on Material Degradation Mechanisms of Artificial Hip Implants Fang ZHOU, Yu YAN, Chunqian XIE, Na LI, Lijie QIAO Corrosion and Protection Center, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, Beijing, China, 100083 Email: yanyu@ustb.edu.cn Abstract: With the increasing interest in Metal-on-Metal (MoM) joint implants, studies have been focused on their wear and corrosion behaviour. Integrated electrochemical tests have been conducted and are reported in this paper. The corrosion, wear and wear-corrosion behaviour for three materials High Carbon CoCrMo, Low Carbon CoCrMo and UNS S31603 have been discussed. Corrosion effects on the overall performance for the three materials are analyzed. Two distinct regimes have been found for the three materials: (a) the running-in regime and (b) the steady state regime, in line with other research. Even in the steady state regime, 20% - 30% of the material degradation can be attributed to corrosion-related damage. High Carbon CoCrMo showed ex- cellent corrosion, wear, corrosion-wear resistance therefore it delivered the best overall performance in terms of a lower wear rate, a lower friction coefficient and higher resistance to corrosion. Keywords: biotribocorrosion; proteins; artificial hip implants; cobalt-alloy wear; debris 腐蚀与摩擦交互作用对人工关节钴合金材料 损失机理的影响 周芳，岩雨，谢春乾，李娜，乔利杰 北京科技大学腐蚀与防护中心，北京，100083 Email: yanyu@ustb.edu.cn 摘 要：由于其相对较低的磨损速率，全金属人工髋关节植入体吸引了越来越多的研究者。研究方向 主要集中于金属与金属所组成的摩擦副的摩擦与腐蚀特性上。但是其中大部分研究都是将机械摩擦磨