模拟深海环境下In元素对Al-Zn-In牺牲阳极活化性能的影响.pdfVIP

The 6th China Corrosion Conference Effect of In Element on the Activation of Al-Zn-In Sacrificial Anode under Simulative Deep Sea Environment Shengnan HU, Tao ZHANG, Yawei SHAO, Guozhe MENG Corrosion and protection Laboratory, College of Materials Science and Chemistry Engineering, Harbin Engineering University, Harbin, China Email: zhangtao@hrbeu.edu.cn Abstract: The performance differences of Al-Zn-In sacrificial anode in shallow water and deep sea water en- vironment were investigated by means of open circuit potential，potentiodynamic polarization, potentiostatic polarization and current efficiency. The results show that the electric quantity capability and current effi- ciency of sacrificial anode decreased in simulative deep sea water environment which compared with shallow water. And the effect degree of oxygen concentration (O2), hydrostatic pressure (P), temperature (T) to sacri- ficial anode is O2 ＜P ＜T. The open circuit potential of sacrificial anode was moved to 150mV negative when 5×10-3 mol/L In3+ was added to artificial sea water,and the current efficiency was decrease in shallow water environment because of self-corrosion which was obviously improved under deep sea water environment. Keywords: Al-Zn-In sacrificial anode; deep sea water environment; In element 模拟深海环境下In 元素对Al-Zn-In 牺牲阳极活化性能的 影响 胡胜楠，张涛，邵亚薇，孟国哲 哈尔滨工程大学，材料科学与化学工程学院，腐蚀与防护实验室，哈尔滨，中国，150001 Email: zhangtao@hrbeu.edu.cn 摘 要：通过对Al-Zn-In 牺牲阳极在不同条件下的进行开路电位、动电位极化、恒电位极化、腐蚀失 重测试，研究了牺牲阳极在表层海水和深海环境下的性能差异，以及氧含量、静水压力、温度变化对 牺牲阳极性能的影响程度。研究结果表明：与表层海水中相比，牺牲阳极在模拟深海环境下的放电量