锰熔融还原渣的泡沫性研究.pdfVIP

上海金属990205 上海金属 SHANGHAI METALS 1999年　第21卷　第2期　Vol.21　No.2　1999 锰熔融还原渣的泡沫性研究 郭曙强　蒋国昌　徐匡迪 　　摘要　用X射线动态显像技术在1300～1450℃的范围内研究了CaO-SiO -MnO渣系的泡沫性，采 2 用单位时间单位气量所产生的泡沫渣量作为泡沫指数描述熔渣的泡沫性。测定了CaF 、FeO、 2 MgO、S及MnO本身对该渣系泡沫性的影响。研究表明渣的泡沫稳定性随着熔渣粘度的增大和表面 张力的减小而增大。 【关键词】　熔融还原　CaO-SiO -MnO渣系　泡沫渣 2 A STUDY ON THE FOAMING CHARACTERS OF SLAG IN MANGANESE SMELTING REDUCTION Guo Shuqiang　Jiang Guochang　Xu Kuangdi （Shanghai University） 　　Abstract　The foaming characters of CaO-SiO2-MnO slag system were studied with X-ray transmission apparatus at temperature ranging from 1300 to 1400 ℃．The foaming slag quantity formed by unit gas within unit interval was used as foaming index to describe slag foaming characters ．The effects of CaF2 ，FeO ，MgO ，S and MnO itself on foaming were studied too．It was found that the stability of slag foaming increased with increasing of viscosity and decreasing of surface tension ． 　　Key Words　Smelting Reduction，CaO-SiO2-MnO Slag System,Foaming Slag 1　前　言 　　熔融还原是当今国际冶金界注目的新技术。在铁浴式熔融还原过程中，主要的反应是渣中氧化 物的还原，从而产生大量的CO、CO 和H O等气体，这些气体要从厚厚的渣层逸出，在某些条件 2 2 下，不可避免地要引起熔渣的泡沫化。在铁浴式反应器内，生成的泡沫渣不仅会占据大部分炉膛空 间，而且还会严重地阻碍二次燃烧产生的热量有效地向下传递给铁浴，严重时甚至发生事故。因而 泡沫渣的控制是熔融还原工艺的关键技术之一。 　　有关铁熔融还原过程中渣的泡沫已有研究 ［1］ ，但未见到有关锰熔融还原过程泡沫渣的研究报 道。本研究的目的是在实验条件下，研究渣成分及温度对锰熔融还原过程CaO-SiO-MnO主渣系泡 2 沫性的影响。 2　实验装置及方法 2.1　实验装置 　　实验是在图1所示的X射线-电视动态显像高温实验装置(简称X－TV实验装置)