单向碳纤维增强复合材料的力学性能分析.pdfVIP

Data Base of Mechanical Properties of Unidirectional Carbon Fiber-Reinforced Polymer Composites 单向碳纤维增强复合材料的力学性能分析 1 1 1 2* Toshi SUGAHARA , Suchalinee MATHUROSEMONTRI , Hiroyuki HAMADA , Yuqiu YANG 1 1 1 2,* 菅原 寿秀 ; 马图劳穆迪 苏查丽妮 ; 滨田 泰以 ； 阳 玉球 1 Department of Advanced Fibro-Science, Kyoto institute of technology, Matsugasaki, Sakyo-ku, Kyoto, 606-8585, Japan 先端纤维科学，京都工艺纤维大学，京都，日本 2 Collage of Textiles, Donghua University, NO.2999 of RD Renmin (N), Songjiang District, Shanghai, 201620, P.R. Chaina 纺织学院，东华大学，上海，中国 *E-mail: amy_yuqiu_yang@ Abstract: This paper reports the database of mechanical properties of unidirectional carbon fiber-reinforced polymer composites. Both of polyamind6 and epoxy resins were used as matrix. The unidirectional carbon prepregs were prepared though the hot melt process and the laminated prepreg sheet were molded to CFRP by compression molding. The mechanical and interfacial properties of both 0 and 90 degree carbon fiber composites were investigated by tensile test. Fracture surfaces were observed by scanning electron microscope. For 0 degree specimens, tensile strength and modulus of CF/Epoxy composites were higher than CF/PA6 composite. The tensile strength of 90 degree specimens revealed the similar results with 0 degree specimens. CF/Epoxy composi