TiC-B-%2c4-C-BN%2fC复合材料抗氧化行为初步的研究.pdfVIP

TiC-B C-BN/C 复合材料抗氧化行为初步研究 4 宋永忠 翟更太 李贵生 刘朗 (中国科学院 山西煤炭化学研究所 山西 太原 030001) 摘要 以煤焦油沥青为粘结剂 煅烧石油焦为填料 Ti B C BN 等为陶瓷填加组元 采 4 用热压成型工艺制备出炭/ 陶复合材料 考察了不同氧化温度材料的失重情况 并分别对材 料在 850 950 和 1000 的恒温氧化行为作了研究 并经计算得出 TiC-B4C-BN/C 复合 材料在 850 1000 的空气中的表观活化能为446kJ/mol 研究表明 TiC-B C-BN/C 复合材 4 料具有良好的抗氧化性能 关键词 TiC-B C-BN/C 复合材料 抗氧化 表观活化能 4 Oxidation Behavior of TiC-B C-BN/C Composite in Air 4 SONG Yong-zhong, ZHAI Geng-tai, LI Gui-sheng, LIU Lang (Institute of Coal Chemistry, Chinese Academy of Science, Taiyuan 030001, China) Abstract: The resultant TiC-B4C-BN/C composite was prepared from starting materials of calcined coke, coal tar pitch, boron carbide, boron nitride and titanium by the hot-pressing process. The effect of oxidation temperature of the composite had been investigated by TG, and its isothermal oxidation behavior at 850 950 and 1000 , respectively, also was investigated , through calculate received apparent activation energy of the composite oxidated with air was 446kJ/mol. The results reveal that: the TiC-B4C-BN/C composite has excellent anti-oxidation. Keywords TiC-B C-BN/C composite; anti-oxidation; apparent activation energy 4 1.前言 炭石墨材料因其具有卓越的高温强度 良好的抗热震性能而广泛地用于各种高温环境 [1-4] 但在氧化气氛中 普通炭石墨材料超过 350 即使高纯石墨材料也在高于 600 就 开始氧化轻则使材料的机械性能大幅度下降 重则使材料失效[5-8] 而一般的陶瓷材料具有 良好的抗氧化性 但其缺点是其较差的抗热震性能 这样大大限制了它的使用范围 为了弥 补他们各自的缺点 许多研究者制备出了各种炭/ 陶复合材料 本文将 TiC[9] B C[ 10] BN[11-13]等具有良好抗氧化性能的陶瓷组元引入到炭材料中