前置过滤器在凝结水系统中应用.pdfVIP

前置过滤器在凝结水系统中的应用 毛惠斌，平先锋 043300 （山西漳泽电力股份公司河津发电分公司，山西河津， ） 摘要：热力系统的腐蚀主要是停机阶段发生的腐蚀，在启机冲洗过程中，由于凝水水质的严 重超标，精处理系统不具备投运条件，导致冲洗过程中水质长时间不达标。一次启动带入热 力系统的铁，相当于正常运行三年的量。增设前置过滤器后提高了水汽品质，防止了冲洗过 程中将杂质带入高低压加热器和汽包、水冷壁造成的危害，而且缩短启机冲洗时间，提高了 机组运行的经济性。 关键词：精处理 过滤器 高速混床 水汽品质 Pretage filters in congealment aqueous system application （Zhangze Power joint-stock company ，Hejin,Shanxi ，043300) Abstract: Thermodynamic systems corrosion is mainly the corrosion which the engine off stage occurs, in opens machine in the flushing process, as a result of condensation water qualitys serious exceeding the allowed figure, the fine processing system does not have throws transports the condition, causes in the flushing process the water quality long time not to attain a designated standard. A start leads thermodynamic systems iron, is equal in a normal operation three year quantity. After additionally building the pretage filter, improved the water vapor quality, prevented in the flushing process to lead the impurity the harm which the high and low pressure heater and the steam drum, the water cooling wall created, moreover reduced opens machine the flush time, enhanced the unit movement efficiency. Key word: Fine processing Filter Mixes the bed high speed Water vapor quality 0 引言 热力系统在检修或冷备状态下，虽然采取了很多防腐蚀的措施，但是由于系统内部状况 的局限性，在热力系统的内表面有不同程度的锈蚀产生。启机过程中，在水流冲刷和热力系 统热胀冷缩的作用下，系统中的氧化铁在机组冷态启动时会进入凝结水系统中，导致启动时 的氧化铁超标严重，如果不及时去除这些固形物，系统水温升高后，固态氧化物又会向溶解 性的物质转变，最终会导致水冷壁管等热力系统结垢加速，引起垢下腐蚀。给化学监督工作 带来极大的困难。通常情况下，往往是不顾及化学监督的要求，强行带负荷，直接后果是导 致热力系统结垢速率增加，影响机组的效率，这种影响是长期的。国内外的研究表明，如果 没有凝结水精处理系统，一次启动带入热力系统的铁，相当于正常运行三年的量。 1 河津发电公司凝结水精处理系统介绍和存在的问题 漳泽电力股份有限公司河津发电分公司（以下简称河津发电分公司）1#、2#机组为2× 350MW汽轮发电机组，日本三菱重工制造，2000年8月和2000年11月相继投入生产。 锅炉主要技术规范