2013 年 9 月 2013 年特钢年会论文集 Sept. 2013 短流程增氮工艺探讨 杨利委 （南京钢铁联合有限公司电炉厂，江苏，41445 南京，210035 ） 摘 要：在短流程生产实践中，对使用高氮含量精炼渣、吹氮气、含氮合金三种增氮方式增氮的可能性和 规律进行探讨，结果表明三种增氮方式都可以起到增氮效果，尤以含氮合金增氮效果明显且可控，三种增 氮方式都需要有与之相匹配的钢种生产工艺流程才能满足连续生产需要。 关键词：增氮，含氮钢，氮气 Increasing Nitrogen Content of Short Flow Route Steelmarking Process to explore Yangliwei (EAF Plant, Nanjing Iron and Steel United Co.,Ltd, Nanjing 210035) Abstract ：In short process production practice, possibility and regularity of useing high nitrogen content in refining slag, blowing nitrogen,and ogen-containing alloy which three kinds of nitrogen increasing ways to be explored ，the results show that three kinds of nitrogen treatment can increase nitrogen effect, especially in the nitrogen alloy increase nitrogen effect is obvious and controllable, three kinds of increasing nitrogen way needs to have matching steel production process to meet the needs of continuous production. Keywords: Increasing Nitrogen ；Steel bearing nitrogen；N2 1. 前言 氮对大多数钢种而言是有害元素，但在部分不锈钢、非调质钢以及一些高韧性结构钢中 却是有益的合金元素。他在钢中的作用主要是可以在轧后或镦后冷却过程中析出细小合金氮 [1] 化物，达到弥散强化的目的，从而提高钢的性能 。 非调质钢利用氮的这一特性，具有节能、简化生产工序及产品质量高等优点，被广泛应 用于汽车连杆、曲轴、驱动轴等零件和结构件。随着汽车行业的迅猛发展，非调质钢将会是 未来一段时间内各个钢铁企业角逐的焦点。因此对增氮工艺的研究对冶金企业的指导意义是 不言而喻的。 102 2013 年 9 月 2013 年特钢年会论文集 Sept. 2013 2. 短流程增氮工艺装备条件 （1）100t 超高功率电弧炉一座，EBT 出钢，冶炼周期 35min ； （2 ）100t LF 精炼炉 2 座，冶炼周期 38min ； （3 ）90tVD 双工位精炼炉 2 座，极限真空度 1mbar； （4 ）5 机 5 流连铸机 1 座，弧半径 8m，断面 150mm×150mm，浇注周期45min ；3 机 3 流连铸机一座，弧半径 12m，断面 320mm×480mm，浇注周期45min 。 3. 增氮工艺方案设计及结果讨论 3.1 使用高氮含量的精炼渣增氮