Q450NQR1高强耐候钢的耐腐蚀性能的研究.pdfVIP

The 6th China Corrosion Conference Study on Corrosion Properties of Q450NQR1 Weathering Steel 1 2 2 1 Xuequn CHENG , Yuqun YIN , Jinbin ZHAO , Xiaogang LI 1Corrosion and Protection Center, Beijing Science and Technology University, Beijing, China 2Research Institute of Nanjing Iron and Steel Company, Nanjing, China Email: Chengxuequn@ustb.edu.cn Abstract: The accelerated corrosion properties of high strength weathering steel Q450NQR1 are studied and compared with mild carbon steel Q345B by means of the periodical immersion cyclic corrosion test. The cor- rosion potential and corrosion current density is analyzed by electrochemical technology. The results show that under the testing conditions the weight losses and average corrosion rates of Q450NQR1 are remarkably lower than those of Q345B. The corrosion product formed on Q450NQR1 is more stable than that on Q345B, the EDS and XRD results suggest that Cu and Cr can improve the stability of corrosion product formed on Q450NQR1, and with the increasing contents of α-FeOOH, the corrosion resistance of Q450NQR1 improved. Keywords: weathering steel; corrosion; railway steel Q450NQR1 高强耐候钢的耐腐蚀性能研究 1 2 2 1 程学群 ，尹雨群 ，赵晋斌 ，李晓刚 1 北京科技大学腐蚀与防护中心，北京，中国，100083 2 南京钢铁股份有限公司研究院，南京，中国，100083 Email: chengxuequn@ustb.edu.cn 摘 要：通过采用周浸腐蚀试验方法研究了Q450NQR1 高强耐侯钢和Q345 钢的耐腐蚀性能，并测试 了不同周浸腐蚀时间后试样的腐蚀电位和腐蚀电流密度。研究发现Q450NQR1 相对Q345 钢有更好的 耐腐蚀性，且其表面的锈蚀产物膜在周浸腐蚀试验48 小时后基本达到稳定。微观腐蚀形貌及EDS 分 析认为这是由于Q450NQR1 钢中的添加的Cu 和C