GCr15钢棒线材碳化物控制.pdfVIP

GCr15 钢棒线材碳化物控制 江运宏 高建荣 （宝钢股份特殊钢事业部，上海 200940 ） 摘 要 本文结合国内外相关的研究成果和实际生产经验，探讨了 GCr15 钢球化机制和球化退火工艺；从退火质 量稳定性等角度出发，对比分析了GCr15钢棒线材的三种不同炉型的球化退火方式及退火工艺；进而对影响球化退 火质量的多种因素作了深入研究，实现了碳化物粒度的有效控制，从而满足了用户不同的使用要求。 关键词 GCr15 钢；棒线材；球化退火；碳化物粒度 Discussion on Spheroidizing Annealing of GCr15 Bearing Steel JiangYunhong GaoJianrong (Baoshan Iron ＆Steel Co.,Ltd. Special Steel business unit, Shanghai 200940, China) Abstract The mechanism of spheroidzation and the selection of annealing process for GCr15 bear steel are discussed in the paper, according to the correlative research civil and abroad and the experience of the productive practice. In the same, analyze and compare the three main spheroidizing annealing mode of GCr15 bearing steel in the paper , based on the production quality stability after annealing .Then, explain the important effect imposed on the spheroidizing annealing quality improvement of bearing steel by the continuous advancement of annealing equipment condition. In the end , bring up the further development direction for the quality of bearing steel in forms of bar and wire civil after spheroidizing annealing. Key words GCr15 bearing steel，bar and wire ; spheroidizing annealing ，carbide particle size 引言 轴承是机械设备中的重要零件之一，使用过程中承受极高的交变载荷、摩擦、腐蚀等，使用条件十分苛 刻。因此对于轴承钢而言，要求具有良好的强韧性配合及较高的接触疲劳性能和耐磨性。GCr15 钢作为轴承 钢的代表钢种，由于其优良的加工性能和使用性能，被广泛应用于制造各种轴承的滚珠、滚柱和套圈等，其 成分自其诞生以来的近一个世纪基本没有变化。据统计，失效的轴承以接触疲劳破坏占第一位，因此其质量 评估一般以接触疲劳寿命来衡量，而影响疲劳寿命的关键因素是钢的纯净度与碳化物的分布、大小与形态[1] 。 随着炉外精炼及真空脱气技术的发展，轴承钢的纯净度大大提高。通过对高温均匀化退火、控轧控冷和球化 退火等方面广泛深入的研究和实践，碳化物的质量水平也在不断提高。 长期以来，以国外 SKF3 和 SAE52100SF 为代表的轴承钢质量一直稳居世界一流水平。而国内自 20 世 纪 80 年代以来，随着冶炼、轧制和热处理等技术装备的不断进步，轴承钢的生产方式有了较大幅度转变， 其中作为控