2014 年全国天然气学术年会 CFRP 用于钢质管道管体缺陷修复的适用性研究 周 祥 （中国石油西南油气田分公司科技信息处） 摘 要:通过大量的室内和现场应用试验，研究了CFRP材料的耐久性，以及CFRP用于钢质管道管体缺陷 修复的电偶腐蚀风险、修复的匹配性和可靠性，为工程应用的设计、选材、成型、维护、检验检测提供了 参考。试验结果表明，CFRP材料具有优异的耐酸碱老化、耐湿热老化及耐候性能，该技术具有传统维修 方法无法比拟的各种优点，具有广阔的应用前景。CFRP与钢管的电偶腐蚀会严重影响修复质量，造成严 重的安全隐患，因此必须采取措施进行防护。 关键词:碳纤维 复合材料 缺陷 修复 质量控制 Applied research for CFRP composite materials rehabilitation Zhou Xiang(Petrochina Southwest Oil Gas Field Company Science Technology Information Application) ABSTRACT: Through massive laboratory experiments and field tests, the durability, the risk of galvanic corrosion, the matching and reliability of CFRP which used for materials rehabilitation were studied. The test results show that the CFRP material has various advantages, and this technology holds great promise, which provides reference for the design, molding, maintenance and inspection. Galvanic corrosion problems will seriously affect the quality of CFRP repair, so we must adopt the measures for protection. SUBJECT HEADINGS: Carbon fiber, Composite material, Defect, Rehabilitation, Quality control 0 引言 钢质管道是我国流体介质传输工程中的主要载体，但在环境(大气、土壤和微生物等)和内输送介质作 用下会发生腐蚀。很多超期服役管道 在大量的管体腐蚀缺陷，严重危害管道本质安全，管道公司每年需 投入大量的资金用于管道系统的维护维修。近年来，一些油气管道修复技术领域的新材料、新工艺在国内 生产现场规 应用，这些新技术、新产品的安全性和适用性是不可忽视的重要问题。 管体缺陷复合材料修复技术是利用增强纤维和基体树脂在管道外形成复合材料补强层，分担管道承受 的载荷，限制管道缺陷处由内压引起的径向膨胀和环向拉伸应力，从而达到恢复管道正常承压能力的目的。 相比较传统的管道修复方法，具有可在不停输状态下实施、施工过程无明火操作、安全快捷等工艺特点， 已成为近几年管道修复技术研究的热点。碳纤维的弹性 量和钢材十分接近，将碳纤维作为增强体 （即称 作者简介：周祥，1981 年生，工程师，大学本科；2003 年毕业于西南石油大学油气储运专业；主要从事安全环保节能领域 的科技管理工作。地址： （610051）四川省成都市成华区府青路一段5 号天然气大厦。电话：028-8604425。 E-mail：zhouxiang@ 445 2014 年全国天然气学术年会 为CFRP），两者协同变形有利于载荷的均匀分布；当CFRP在承受较大拉应力时，所产生的轴向应变极小 （远 小于管体变形），非常有利于限制管道受压膨胀所引起的径向应变。 CFRP具有比强度高、比 量高、耐疲劳性优良、性能稳定和易于整体成型等许多优异特性, 在