端异氰酸酯聚醚增韧环氧树脂固化动力学研究.pdfVIP

端异氰酸酯聚醚增韧环氧树脂固化动力学研究 　　　　　　　　　　　　　　　　　　　　　ZHANJ IE 　200 1 , 22 ( 6) 端异氰酸酯聚醚增韧环氧树脂固化动力学研究 王庭慰 　陈瑞珠 　赵 　刚 (南京化工大学高分子系 ,南京市 2 10009) ( ) 摘要 　采用差示扫描量热 DSC 技术测定了在芳胺类为固化剂的条件下 ,增韧环氧体系固化反应过程中的热 　　 行为 。得出固化反应过程的动力学参数 ,实验数据表明: 以芳胺为固化剂的体系中 , 固化反应表观活化能及动力学 频率因子 ,反应级数均有明显降低 。 关键词 　环氧树脂 　端异氰酸酯聚醚 　DSC 　反应动力学 St udy on cro sslink kinetics of epoxy resin modified by isocyanate terminated polyet her Wang Tingwei 　Chen Ruizhu 　Zhao Gang (Nanjing University of Chemical Technology ,Nanjing 2 10009) Abstract 　The heat effect s of curing kinetics of various toughed epoxy resin composites wit h aromatic amine crosslinking agent were investigated by t he DSC technology ,and kinetic p arameters of curing reaction were derived . The exp erimental result s show t he app arent activation energy ,kinetic frequency factor and reaction order were obviously de creased ,and t his exp erimental met hod can be used for epoxy curing technology . Keywords 　Epoxy resin 　DSC 　Isocyanate terminated polyet her 　Reaction kinetics 1 　前言 自20 世纪 60 年代以来 , 国内外开展了用各种 2 　实验部分 液态聚合物增韧环氧树脂的研究工作 , 以期在热性 2 1 　实验原料 能、模量及电性能下降不大的情况下 ,提高环氧树脂 聚醚 ,N2 10 、N220 、N204 ,工业品 , 金陵石化公 [ 1 ] ( ) 的韧性 。目前 ,用于环氧树脂增韧的主要方法有 司 ;聚四氢呋喃 ,工业品; 甲苯二异氰酸酯 TD I ,工 2 类 :一为改善环氧树脂本身的韧性 ,增加交联点之 业品;环氧树脂 ,E - 5 1 ,无锡树脂厂 ; 固化剂 E ,芳胺 ( 间的长度 如采用高分子量环氧树脂和大分子固化 类 , 自制 ;端氨基聚醚 , 自制 。 ) ( 剂 ,增加交联点间的柔韧性 如使用具有柔性主链 D SC 分析在 Perkin