1050铝合金板带的多能场非对称铸轧（英文版）.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 2815−2823 Asymmetric cast-rolling of 1050 aluminum alloy strip under multi-energy field 1,2 2 2 Chen SHI , Da-heng MAO , Zong-li FU 1. School of Materials and Engineering, Central South University, Changsha 410083, China; 2. State Key Laboratory of High Performance and Complex Manufacturing, Central South University, Changsha 410083, China Received 28 October 2013; accepted 22 February 2014 Abstract: Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster (d400 mm×500 mm), and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is (13±1) Hz, ultrasonic power is 200 W and ultrasonic frequency is (20±0.2) kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively. Key words: aluminum alloy 1050; asymmetric cast-rolling; multi-energy field; microstructure; mechanical properties of process co