提升热轧产品质量热轧精整技术.pdfVIP

提升热轧产品质量的热轧精整技术 作者：丁文红 摘要：随着热轧技术的发展，“以热代冷”的市场需求越来越强烈，然而，热轧产品高的残余应力水平、 残留氧化物造成的表面质量缺陷以及吕德斯带等问题制约热轧板的广泛应用，对高强钢而言，上述问题更 为严重。本文从机理上对上述质量缺陷产生的原因进行了分析，并提出了针对性的技术解决方案。 Key words: 热轧产品质量、热轧精整技术、残余应力、高强钢 Improve the quality of hot rolled products finishing technology Author ：Ding Wenhong Abstract: With the development of hot rolling technology, market demand of “Substituting hot rolled products for cold rolled products” becomes increasingly urgent. However, there are quite a lot of unsatisfactories and inadequateness of the products existing in the hot rolling products. Such as high level of residual stress, surface defect, Luders band and so on. On high strength steel, these problems are more serious. In this paper, the mechanism on the causes of these problems is analyzed, and put forward specific technical solutions. Key words: quality of hot rolled products, temper mill , flattener 1. 问题的提出 随着热轧技术的发展，热轧薄板的性能和质量不断提高,加之热轧产品的成本优势，使 越来越多的冷轧带钢市场为热轧带钢所取代，特别是在厚度小于2.Om m的热轧薄带钢领域以 及高强度级别的带钢领域，这一趋势尤为明显。为了满足这一市场需求，许多冷轧厂纷纷增 设热轧平整机组，以期在平直度、表面质量，几何外形尺寸，机械性能等方面获得更强的市 场竞争力。 然而从目前已经投产和在建的热轧平整机组来看，平整后的带钢在平直度、机械性能等 方面均得到改善，但对于产品的表面质量以及残余应力问题却显得力不从心，特别是在高强 度级别的热轧带钢领域，这一问题显得尤为突出，并常由此导致下游用户的质量异议；由氧 化铁皮二次压入而造成产品表面的麻点缺陷也直接影响热轧产品的后续应用。虽然多数热轧 平整机组上都配置了昂贵的除尘系统，由于所配置的除尘系统与机组生产时产生的粉尘匹配 度低，而且由于在开卷机、矫直机、平整机等多处均产生氧化铁皮碎片和粉尘，除尘系统配 置缺乏针对性，造成投入大量资金却无法解决问题的局面。此外，横折缺陷也是热轧产品的 常见缺陷。上述问题，无疑减缓了“以热带冷”的进程。 针对上述问题，中冶南方工程技术有限公司自主研发了多功能高品质热轧平整技术，在 原有热轧平整机组上增设氧化铁皮处理工艺段以及残余应力处理工艺段，使热轧平整机组的 产品质量在表面质量、残余应力水平两个关键指标上得到进一步提升，做到产品高品质；使 轧辊、矫直辊、以及机组重要零部件的消耗进一步降低，做到生产低成本；降低对操作人员 的健康损害、对环境的污染，做到环境无损害。在钢铁企业竞争日趋严重的今天，力求在产 品质量、生产消耗、环境压力等方面为钢铁生产企业增加竞争力。 2. 热轧精整机组的工艺配置 中冶南方工程技术有限公司研发的多功能高品质热轧平整机组如图1所示。其设备组成 以及技术装备水平不在此赘述，仅就其新增的工艺功能作一介绍。 图1：多功能高品质热轧平整机组 针对目前热轧平整机组在实际生产中存在的质量问题，即残余应力较大造成后续加工的 质量缺陷；氧化铁皮的二次压入严重，制约热轧板表面质量的提高，中冶南方工程技术有限 公司在热轧精整机组中配置了三个工艺段，即第一工艺段：氧化铁皮处理段；第二工