AuCu3亚格子系统的合金基因Gibbs能配分函数和平衡全息网络相图（英文版）.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 3585−3610 Alloy gene Gibbs energy partition function and equilibrium holographic network phase diagrams of AuCu3-type sublattice system 1,2,3 4 1,2,3 5 6 You-qing XIE , Xiao-bo LI , Xin-bi LIU , Yao-zhuang NIE , Hong-jian PENG 1. School of Materials Science and Engineering, Central South University, Changsha 410083, China; 2. Powder Metallurgy Research Institute, Central South University, Changsha 410083, China; 3. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China; 4. College of Materials Science and Engineering, Xiangtan University, Xiangtan 411105, China; 5. School of Physical Physics and Electronics, Central South University, Changsha 410083, China; 6. School of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China Received 5 September 2014; accepted 5 November 2014 Abstract: Taking AuCu -type sublattice system as an example, three discoveries have been presented: First, the third barrier 3 hindering the progress in metal materials science is that researchers have got used to recognizing experimental phenomena of alloy phase transitions during extremely slow variation in temperature by equilibrium thinking mode and then taking erroneous knowledge of experimental phenomena as selected information for establishing Gibbs energy function and so-called equilibrium phase diagram. Second, the equilibrium holographic network phase diagrams of AuCu3-type sublattice system may be used to describe systematic correlativity of the c