Diffusion bonding of Ti-6Al-4V by pulse current heating and hot-pressing HE Dai-hua(何代华), FU Zheng-yi(傅正义), WANG Wei-min(王为民) State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China Received 28 July 2006; accepted 15 September 2006 Abstract: Pulse current heating (PCH) was used to join Ti-6Al-4V alloy at two cases of with die and without die. Hot-pressing (HP) method was used to provide a comparison between the two methods. Microstructures near the contacting surfaces were observed in optical microscope. Temperature distribution was analyzed. After joining, the tensile properties of the samples were evaluated. Experimental results show that grains and phases grow transversely on contacting surfaces, which makes two parts into a whole with a certain of tensile strength. PCH joining is a different temperature joining method. The highest temperature is located at the interface. The comparison of tensile strengths of samples joined by the two methods indicates that joining temperature and holding time needed by PCH are lower and less than those needed for HP. Key words: pulse current heating; Ti-6Al-4V; joining; hot-pressing; temperature distribution purification of the surface of particle and sintering 1 Introduction activity; and fast sintering at low temperatures[3]. There are many reports on the fabrication of ceramics by this Ti-6Al-4V, an α+β beta alloy, is an important alloy, technique (oxides, S